非晶碳化硅量子点的制备及其光学性质研究

发布时间：2018-03-19 09:41

  本文选题：碳化硅　切入点：脉冲激光烧蚀法　出处：《硅酸盐通报》2017年02期 　论文类型：期刊论文

【摘要】：采用脉冲激光烧蚀法,以多晶3C-SiC陶瓷片为靶材,制备了悬浮于去离子水中的非晶SiC纳米颗粒。利用透射电子显微镜(TEM)、高分辨透射电子显微镜(HRTEM)、傅里叶变换红外吸收光谱(FTIR)、紫外可见吸收光谱(UV-Vis)和光致发光谱(PL)等测试手段对其形貌、结构和光学性质进行了分析。结果表明:这些纳米颗粒由大量的非晶SiC构成,粒径在8~9 nm,光学带隙为3.28 e V;样品表现出较强的光致发光,发光峰位于415 nm处,这主要是由于量子限制效应造成的。
[Abstract]:Using pulsed laser ablation method in polycrystalline 3C-SiC ceramic target and amorphous SiC nanoparticles were prepared in deionized water suspension. Using transmission electron microscopy (TEM), high resolution transmission electron microscopy (HRTEM), Fu Liye transform infrared spectroscopy (FTIR), ultraviolet visible absorption spectroscopy (UV-Vis) and photoluminescence (PL) measurements on the morphology, structure and optical properties were analyzed. The results show that these nanoparticles composed of amorphous SiC composition, particle size in 8~9 nm, the optical band gap of 3.28 e V; samples showed a strong photoluminescence emission peak at 415. Nm, this is mainly due to the quantum confinement effect caused.

【作者单位】： 宿迁学院信息工程学院;南京邮电大学电子科学与工程学院;
【基金】：国家自然科学基金资助项目(61474096) 江苏省高校自然科学基金资助(15KJD140005) 宿迁市科技计划项目资助(S201511) 江苏省青蓝工程资助 宿迁学院科研基金项目资助(2015KY10) 江苏省333工程科研项目资助(BRA2016262)
【分类号】：TQ163.4;TB383.1

【相似文献】

相关期刊论文 前10条

1 季雷华;高素莲;张斌;;量子点的合成、毒理学及其应用[J];环境化学;2008年05期

2 王富;刘春艳;;发光碳量子点的合成及应用[J];影像科学与光化学;2011年04期

3 伊魁宇;王猛;邵明云;;量子点作为离子探针的分析应用[J];广州化工;2012年11期

4 罗慧;李曦;方婷婷;刘鹏;;量子点的毒性研究进展[J];材料导报;2013年19期

5 田瑞雪;武玲玲;赵清;胡胜亮;杨金龙;;碳量子点的氨基化及其对发光性能的影响[J];化工新型材料;2014年01期

6 ;“量子点”晶体将推动部分物理工艺的进步[J];光机电信息;2002年10期

7 徐万帮;汪勇先;许荣辉;尹端l，

本文编号：1633709