两种硼硅酸微晶玻璃制备方法的对比研究

发布时间：2018-04-14 23:07

  本文选题：偏硼酸盐 + 两步法烧结、成瓷性能、玻璃陶瓷　； 参考：《中国电子科学研究院学报》2017年02期

【摘要】：采用偏硼酸盐和硼酸-氧化物为原料,分别通过一步法和两步法制备B_2O_3-SiO_2系微晶玻璃陶瓷材料,并对不同原料和方法制备的陶瓷材料进行XRD、SEM分析及力学、热学性能对比测试。结果表明以偏硼酸盐为原料使用一步法制备硼硅酸盐微晶玻璃陶瓷成瓷性能较两步法制备微晶玻璃陶瓷性能差,两步法制备微波玻璃陶瓷材料玻璃相相对较多,性能较好。
[Abstract]:Using metaborate and boric acid-oxide as raw materials, B_2O_3-SiO_2 glass-ceramics were prepared by one-step method and two-step method respectively. The different raw materials and methods were analyzed by XRD-SEM, and the mechanical and thermal properties were compared.The results show that the ceramic forming properties of borosilicate glass-ceramics prepared by one-step method using metaborate as raw material are worse than that of two-step glass-ceramics prepared by two-step method. The glass phases of microwave glass-ceramics prepared by two-step method are more than those of microwave glass-ceramics, and the properties are better.
【作者单位】： 中国电子科技集团公司第十三研究所;
【分类号】：TQ171.733

【相似文献】

相关期刊论文 前10条

1 牛智勇;向阳;;邯郸制成微晶玻璃陶瓷[J];河北陶瓷;1984年03期

2 王永贤;;微晶玻璃陶瓷复合板的毛板质量控制[J];佛山陶瓷;2006年03期

3 史杰;孙树江;;微晶玻璃陶瓷复合板生产过程中的缺陷及其控制研究[J];佛山陶瓷;2009年07期

4 戴长禄;杨勇;杨明;陈本信;;铜红微晶玻璃陶瓷复合板的研制[J];佛山陶瓷;2009年08期

5 戴长禄;杨勇;杨明;;微晶玻璃陶瓷复合板的发展现状与前景[J];佛山陶瓷;2009年02期

6 胡俊;区卓琨;梁以流;周曦亚;;提高微晶玻璃陶瓷复合板硬度的途径[J];陶瓷;2012年04期

7 吴小福;微晶玻璃陶瓷复合板变形原因浅析[J];佛山陶瓷;2005年09期

8 樊震坤;石汝军;任允鹏;刘宝英;刘德军;赵林;;β-硅灰石微晶玻璃陶瓷高硬度复合板的研制[J];中国陶瓷;2007年04期

9 蒋洋;成惠峰;赵金平;朱中兵;徐健;;整体法制备微晶玻璃陶瓷复合板材[J];中国建材科技;2009年03期

10 吴小福;;微晶玻璃陶瓷复合板色差缺陷[J];佛山陶瓷;2006年06期

相关重要报纸文章 前10条

1 郑惠荣;微晶玻璃陶瓷[N];中国建材报;2003年

2 本报记者 张亚楠;微晶玻璃陶瓷复合板：工艺混搭的时代新宠[N];中国建材报;2014年

3 叶恒青 吴小福;微晶玻璃陶瓷复合板工艺现状及前景展望[N];广东建设报;2005年

4 吴小福;生产微晶玻璃陶瓷复合板的四项基本条件[N];广东建设报;2005年

5 吴小福;微晶玻璃陶瓷复合板变形成因浅析[N];广东建设报;2005年

6 北京德然陶瓷技术有限公司高级工程师 戴长禄;第二代微晶玻璃陶瓷复合砖生产技术[N];广东建设报;2004年

7 吴小福;微晶玻璃陶瓷复合板坯层剥离释疑[N];广东建设报;2005年

8 吴小福;微晶玻璃陶瓷复合板双曲线晶化烧结精确控制工艺[N];广东建设报;2005年

9 吴小福;微晶玻璃陶瓷复合板坯层剥离释疑[N];广东建设报;2005年

10 史晓陵;微晶玻璃陶瓷复合板材[N];中国建材报;2003年

，

本文编号：1751417