电沉积Ni-W梯度镀层及耐磨性研究

发布时间：2018-05-02 16:49

  本文选题：Ni-W梯度镀层 + 硬度　； 参考：《摩擦学学报》2017年03期

【摘要】：通过电沉积技术并调节镀液中镍钨离子配比浓度在铝合金基体表面制备了Ni-W梯度镀层,研究了镀层中W质量分数的变化对梯度镀层性能的影响.结果表明:所制备梯度镀层表面均匀平整,与基体结合良好,沿镀层生长方向W质量分数逐层增加;相比于Ni-W均质合金,Ni-W梯度镀层具有较低的摩擦系数,磨损形貌较为平整,表面剥落少,表现出较好的耐摩擦磨损性能.
[Abstract]:Ni-W gradient coating was prepared on aluminum alloy substrate by electrodeposition and adjusting the concentration of nickel and tungsten ions in the bath. The effect of W content in the coating on the properties of gradient coating was studied. The results show that the gradient coating has a smooth surface, good bonding with the substrate, and the W mass fraction increases layer by layer along the growth direction of the coating. Compared with the Ni-W homogeneous alloy Ni-W gradient coating, the wear morphology of the gradient coating has a lower friction coefficient, and the wear morphology of the gradient coating is flatter than that of the Ni-W homogeneous alloy Ni-W gradient coating. The surface has less peeling and shows better friction and wear resistance.
【作者单位】： 武警工程大学装备工程学院;
【分类号】：TQ153

【相似文献】

相关期刊论文 前6条

1 韩啸;陈吉;孙冬来;吴新春;叶珊珊;;脉冲电流密度对Ni-W合金镀层耐蚀性的影响[J];电镀与环保;2014年04期

2 成生伟;田文怀;;电铸Ni-W合金热压缩变形的流变行为[J];中国有色金属学报;2013年01期

3 李庆伦,杨中东,赵祖欣;Ni-W合金镀膜析出硬化的研究[J];材料保护;1999年07期

4 王宏智,姚素薇,邢冬梅,张卫国;Ni-W纳米结构梯度镀层的制备、表征及热应变特性[J];物理化学学报;2002年11期

5 王志涛;李秀梅;牛艳玲;;电镀Ni-W合金的研究现状及发展趋势[J];通化师范学院学报;2012年02期

6 ;[J];;年期

，

本文编号：1834710