一种高纯沉淀碳酸钙的制备方法

发布时间：2018-05-06 22:05

  本文选题：沉淀碳酸钙 + 氯化钙溶液　； 参考：《无机盐工业》2017年09期

【摘要】：正本发明公布了一种高纯沉淀碳酸钙的制备方法。具体步骤:1)以含有碳酸钙的矿物为原料,煅烧后得到含有氧化钙的产物;2)产物用氯化铵溶液洗脱;3)洗脱后得到氯化钙溶液,分离溶液中的不溶性组分;4)对氯化钙溶液进行碳化,分离碳化后得到的沉淀碳酸钙。实验得到的沉淀碳酸钙纯度95%,其他杂质质量分数0.5%,BET比表面积为3.5~12.5 m~2/g,TAPPI白度为95%~99%,光反射率为96%~99%,黄色指数为
[Abstract]:The original invention discloses a preparation method of high-purity precipitated calcium carbonate. Specific step 1) from minerals containing calcium carbonate as raw materials, calcined to produce a product containing calcium oxide, the product is eluted with ammonium chloride solution to get calcium chloride solution, separation of the insoluble component in the solution 4) carbonization of calcium chloride solution, Precipitated calcium carbonate obtained by separation and carbonization. The purity of the precipitated calcium carbonate is 95%, the other impurity content is 0.5% and the specific surface area of BET is 3.5% 12.5 mm2. The whiteness of TAPPI is 95%, the reflectivity of light is 96% 9999, and the yellow index is 95%.
【分类号】：TQ132.32-18

【相似文献】

中国期刊全文数据库 前10条

1 徐肇锡;;美国兴建沉淀碳酸钙装置[J];无机盐工业;1986年03期

2 ;沉淀碳酸钙[J];技术与市场;1997年12期

3 罗桂甫,陈兰惠;利用沉淀碳酸钙生产装置直接制取超细活性碳酸钙[J];长沙电力学院学报(自然科学版);1999年03期

4 李占远;;添加剂对沉淀碳酸钙粒子形成的影响[J];煤炭与化工;2013年08期

5 宋耘;洪杏生;胡海鸿;;《沉淀碳酸钙(轻质)》国家标准简介[J];化工标准化;1985年03期

6 胡庆福;胡金秀;李保林;;年产万吨沉淀碳酸钙厂工艺设计[J];河北化工;1985年03期

7 孙世泽;;沉淀碳酸钙的加压碳化[J];河南化工;1987年04期

8 ;沉淀碳酸钙的制备[J];无机盐工业;1996年03期

9 袁伟,金鑫;纸张涂布用片状沉淀碳酸钙的研制[J];精细化工;1998年02期

10 胡庆福,胡晓波,宋丽英,刘宝树;沉淀碳酸钙制造及其改性处理技术[J];非金属矿;1999年02期

中国重要会议论文全文数据库 前2条

1 金日光;张毅;马秀清;;一种高速涡流剪切法制备超微沉淀碳酸钙的方法[A];纳微粉体制备与应用进展——2002年纳微粉体制备与技术应用研讨会论文集[C];2002年

2 ;活性沉淀碳酸钙的清洁生产[A];2005年全国钙镁盐行业会议文集[C];2005年

中国硕士学位论文全文数据库 前1条

1 吴晓萍;芽孢杆菌沉淀碳酸钙的影响因素[D];中国地质大学;2013年

，

本文编号：1854087