从电镀含镍污泥中回收硫酸镍的工艺

发布时间：2018-05-10 04:42

  本文选题：电镀废水 + 污泥　； 参考：《电镀与涂饰》2017年13期

【摘要】：针对揭阳某电镀园区处理电镀废水所产生的含镍污泥,提出纯水洗涤后电解提纯的硫酸镍回收工艺,确定了最佳工艺参数如下:洗涤水量是含镍污泥的3.5倍,洗涤搅拌18 min,洗涤后静置30 min;电解时电流密度为0.02~0.06 A/dm~2,电压约1 V,时间1 h。可以得到质量分数约6%的硫酸镍溶液,其纯度满足电镀镍槽液直接补充的需要,实现了污泥的无害化及资源化处理,并具有一定的经济效益。
[Abstract]:According to the nickel - containing sludge generated in the treatment of electroplating wastewater in an electroplating park , the optimum parameters are as follows : washing water is 3.5 times of the nickel - containing sludge , the washing is stirred for 18 min , the washing is allowed to stand for 30 min , the current density is 0.02 - 0.06 A / dm ~ 2 at the time of electrolysis , the voltage is about 1 V and the time is 1 h . The purity of the nickel sulfate solution with the mass fraction of about 6 % can be obtained . The purity of the nickel sulfate solution can meet the requirement of direct replenishment of the plating nickel bath solution , thus realizing the harmless and resource treatment of the sludge and having certain economic benefits .

【作者单位】： 广东环协科技咨询开发中心;揭阳市表面处理生态园有限公司;
【分类号】：TQ138.13;X781.1

【参考文献】

相关期刊论文 前1条

1 胡铁骑,左丹江,范定义,谭沛真;中国电镀行业的发展与不平衡[J];材料保护;2000年02期

【共引文献】

相关期刊论文 前4条

1 刘玉兵;蒋小友;;从电镀含镍污泥中回收硫酸镍的工艺[J];电镀与涂饰;2017年13期

2 蒋小友;吴军;;利用电镀酸铜废渣修复碱铜阳极的方法[J];电镀与涂饰;2015年12期

3 吴益文;楚民生;华沂;胥成明;初敏;徐凌云;蔡政;;镀铬钢板表面微观缺陷对其所包装食品的影响[J];检验检疫科学;2008年06期

4 张学元,韩恩厚,李洪锡;中国的酸雨对材料腐蚀的经济损失估算[J];中国腐蚀与防护学报;2002年05期

【相似文献】

相关期刊论文 前10条

1 方宗豪,林志业;结晶硫酸镍的生产[J];有色冶炼;1983年01期

2 陈建p，

本文编号：1867834