压缩玻璃碳的基础研究取得重要进展

发布时间:2018-05-29 02:41

  本文选题:玻璃碳 + 石墨相 ; 参考:《机床与液压》2017年14期


【摘要】:正碳具有石墨、金刚石、富勒烯、碳纳米管、石墨烯等多种同素异形体,石墨在高压下可直接转变成超硬金刚石。对于这种高温高压截获的亚稳相,其晶体结构与初始前驱体结构、压力温度条件以及加载或卸载方式密切相关,为探索新奇碳材料提供了机会。亚稳材料制备技术与科学国家重点实验室(燕山大学)田永君教授、赵智胜教授等人与国内外科学家合作,以玻
[Abstract]:Normal carbon has many isomorphism such as graphite, diamond, fullerene, carbon nanotube, graphene and so on. Graphite can be transformed into super hard diamond directly under high pressure. For the metastable phase intercepted at high temperature and high pressure, the crystal structure is closely related to the initial precursor structure, the pressure and temperature conditions, and the loading or unloading mode, which provides an opportunity for exploring novel carbon materials. Professor Tian Yongjun, Professor Zhao Zhisheng, State key Laboratory of preparation Technology and Science of Metastable Materials (Yanshan University), and others have cooperated with scientists at home and abroad.
【分类号】:TQ127.11

【相似文献】

相关期刊论文 前5条

1 ;玻璃碳试制情况汇报[J];电碳技术;1976年02期

2 王君林;玻璃碳表面氧化行为[J];东北师大学报(自然科学版);2000年04期

3 王君林,关振中;玻璃碳制备过程中的结构分析[J];东北师大学报(自然科学版);1995年03期

4 王君林,黄可心,孙国恩,邹广田;玻璃碳结构形成过程分析[J];东北师大学报(自然科学版);1998年04期

5 柯泽豪;胡宪霖;丁志明;张营煌;;类玻璃炭孔隙结构的TEM考察(英文)[J];新型炭材料;2005年04期

相关会议论文 前1条

1 王君林;王群;杨海滨;邹广田;;玻璃碳制备过程的Raman光谱分析[A];第三届中国功能材料及其应用学术会议论文集[C];1998年



本文编号:1949184

资料下载
论文发表

本文链接:https://www.wllwen.com/kejilunwen/huaxuehuagong/1949184.html


Copyright(c)文论论文网All Rights Reserved | 网站地图 |

版权申明:资料由用户ae6fd***提供,本站仅收录摘要或目录,作者需要删除请E-mail邮箱bigeng88@qq.com