发布时间：2018-06-02 00:03

  本文选题：中间相炭微球 + 中温沥青　； 参考：《炭素技术》2017年05期

【摘要】：以自烧结性较差的MCMB为原料,四氢呋喃作为溶剂,采用溶液混合法对MCMB进行沥青改性以提高其烧结性能。考察了沥青含量对MCMB制备的石墨材料结构和性能的影响。实验结果表明:随着沥青含量的增加,石墨材料的结构变得更加致密,体积密度、弯曲强度和肖氏硬度都随着沥青含量的增加先增大后减小。在沥青含量为18%时达到最大值,体积密度为1.96 g/cm~3,弯曲强度为62.6 MPa,肖氏硬度为55.9。石墨材料的电阻率在14.8~21.8μΩ·m范围内并随着沥青含量的增加而减小。
[Abstract]:The bitumen of MCMB was modified by solution mixing method with MCMB as raw material and tetrahydrofuran as solvent in order to improve its sintering performance. The effect of asphalt content on the structure and properties of graphite prepared by MCMB was investigated. The experimental results show that with the increase of asphalt content, the structure of graphite material becomes denser, the bulk density, bending strength and Shore hardness all increase first and then decrease with the increase of asphalt content. When the asphalt content is 18, the volume density is 1.96 g / cm ~ (-3), the bending strength is 62.6 MPA, and the Shore hardness is 55.9. The resistivity of graphite is in the range of 14.8 渭 惟 m and decreases with the increase of asphalt content.
【作者单位】： 湖南大学材料科学与工程学院;湖南省高性能炭石墨材料工程技术研究中心;湖南省长宇新型炭材料有限公司;
【基金】：湖南省战略性新兴产业重大核心技术类项目(2015GK1025)
【分类号】：TQ127.11

【相似文献】

相关期刊论文 前10条

1 景立圯;;高应变石墨的研究[J];炭素技术;1990年03期

2 陈振山;碳石墨材料的耐腐蚀性能[J];电碳技术;1981年01期

3 邱海鹏,郭全贵,宋永忠,翟更太,宋进仁,刘朗;石墨材料导热性能与微晶参数关系的研究[J];新型炭材料;2002年01期

4 叶麟;石墨化升温曲线的研究[J];炭素;2005年02期

5 邓念;袁观明;别望望;董志军;张贵萍;赵杰;李轩科;;细粒石墨材料的热压制备[J];武汉科技大学学报;2010年04期

6 解胜利;浸渍对炭-石墨材料孔隙孔径的影响[J];炭素技术;2000年03期

7 徐迎节;;超低灰无烟煤石墨化产品的生产及应用[J];煤炭加工与综合利用;2013年03期

8 杜林虎,陈大明,潘伟,陈健;超声波对鳞片状石墨的粉碎作用及结构影响[J];硅酸盐通报;2000年04期

9 M.Kakuta;晨雨;;煅后焦性质和以它们为骨料制备的石墨化棒性质之间的关系[J];炭素技术;1986年04期

10 ;超高强石墨材料[J];中国搪瓷;1998年05期

相关会议论文 前1条

1 李明宇;李平;张启彪;鲍彬;;我国光伏发电与硅晶体生长用等静压石墨[A];第22届炭—石墨材料学术会论文集[C];2010年

相关硕士学位论文 前1条

1 史学敏;连续式石墨化电炉冷却系统的优化设计及数值模拟[D];东北大学;2011年

，

本文编号：1966322