熔盐法和柠檬酸盐法对LSCF烧结活性的影响

发布时间：2018-06-02 12:47

  本文选题：无机非金属材料 + 熔盐法　； 参考：《电源技术》2017年06期

【摘要】：分别采用熔盐法和柠檬酸盐法制备了组成为La_(0.6)Sr_(0.3)Co_(0.3)Fe_(0.7)O_(3-δ)的固体氧化物燃料电池(SOFC)阴极粉体材料,对比了二者的烧结活性,并对粉体粒度分布和表面活性进行了表征。结果发现柠檬酸盐法合成的粉体具有更高的烧结活性。粒度分析实验表明柠檬酸盐法合成粉体的一次颗粒尺寸比熔盐法大约小了一个数量级;吸附性能实验表明柠檬酸盐法合成的粉体具有更强的吸附能力。较小的颗粒尺寸和较高的粉体表面能使得柠檬酸盐法合成的粉体具有更高的烧结活性。
[Abstract]:The cathode powder materials of solid oxide fuel cell (SOFC- 未) consisting of La _ S _ (0.6) O _ (3) C _ (3) and C _ (3) C _ (3) were prepared by molten salt method and citrate method, respectively. The sintered activity of the two materials was compared, and the particle size distribution and surface activity of the powder were characterized. The results showed that the powders synthesized by citrate method had higher sintering activity. The particle size analysis shows that the primary particle size of the synthesized powder is about one order of magnitude smaller than that of the molten salt method, and the adsorption property experiment shows that the powder synthesized by the citrate method has a stronger adsorption capacity. The smaller particle size and higher surface energy of the powders make the powders synthesized by citrate method have higher sintering activity.
【作者单位】： 武汉科技大学化学与化工学院;湖北省煤转化与新型碳材料重点实验室;
【基金】：国家自然科学基金项目(21206129)
【分类号】：TM911.4

【相似文献】

相关期刊论文 前10条

1 ;一种高烧结活性氧化铝粉体的制备方法[J];无机盐工业;2003年01期

2 ;高烧结活性陶瓷前驱粉体制备成功[J];现代科学仪器;2013年04期

3 ;宁波材料所合成高烧结活性的石榴石相纳米粉体[J];人工晶体学报;2013年08期

4 王卫民;魏少红;赵双会;王留昌;李文博;;溶胶-凝胶干燥工艺对粉体烧结活性的影响研究[J];信阳师范学院学报(自然科学版);2008年04期

5 金公;用反应喷雾法制取钨基合金[J];兵器材料科学与工程;1992年08期

6 李戬;童世合;;燃烧法制备镁铝尖晶石粉体及其烧结活性研究[J];耐火材料;2011年03期

7 刘志辉;关翔锋;张s，

本文编号：1968817