聚偏氟乙烯乳液改性砂浆的性能研究

发布时间：2018-06-22 02:29

  本文选题：聚偏氟乙烯乳液 + 改性砂浆　； 参考：《新型建筑材料》2017年08期

【摘要】：聚合物可以显著改善水泥基材料的工作性、抗弯拉强度及耐腐蚀等性能。研究不同聚灰比(P/C)下,聚偏氟乙烯乳液对水泥砂浆工作性能、力学性能及长期耐久性能的影响。结果表明:聚偏氟乙烯乳液对水泥砂浆具有减水作用,且保水及粘聚性较好,同时具有一定的引气性;可提高砂浆的变形能力,改善脆性大的缺陷,增加砂浆的拉伸粘结强度;提高砂浆的抗氯离子渗透能力,且吸水率降低、抗收缩性能提高。
[Abstract]:Polymer can significantly improve the workability, flexural tensile strength and corrosion resistance of cement-based materials. The effects of polyvinylidene fluoride (PVDF) emulsion on the working properties, mechanical properties and long-term durability of cement mortar at different P / C ratios were studied. The results show that polyvinylidene fluoride emulsion has water reducing effect on cement mortar, good water retention and cohesion, and good air entrainability, which can improve the deformation ability of mortar, improve the defect of high brittleness and increase the tensile bond strength of mortar. The resistance to chloride ion penetration of mortar is improved, and the water absorption rate is decreased, and the shrinkage resistance is improved.
【作者单位】： 山东华伟银凯建材科技股份有限公司;
【分类号】：TQ177.62

【相似文献】

相关期刊论文 前10条

1 郑凤;黄征青;;聚偏氟乙烯有机-无机超滤膜性能影响因素的研究进展[J];化学与生物工程;2010年06期

2 刘双进;王静荣;刘福谅;;聚偏氟乙烯超滤膜的研究[J];膜科学与技术;1981年02期

3 邵平海，，孙国庆;聚偏氟乙烯微滤膜亲水化处理[J];水处理技术;1995年01期

4 吴世清;;化工标准化动态[J];化工生产与技术;2013年03期

5 姜福昌;;探索以氟聚合物解决化工过程中的难题[J];含氟材料;1980年03期

6 李争彩;林书玉;;聚偏氟乙烯的性能以及和压电陶瓷的比较[J];菏泽学院学报;2007年02期

7 王静荣;聚偏氟乙烯大孔超滤膜的研究[J];环境科学;1995年01期

8 ;文题录[J];含氟材料;1981年03期

9 赵玉杰;;聚偏氟乙烯平板膜处理MgCl_2水溶液的实验研究[J];四川化工;2012年03期

10 曹江;钟乐;湛含辉;;纳米二氧化钛和羟甲基纤维素对聚偏氟乙烯超滤膜结构和性能的影响[J];湖南工业大学学报;2009年03期

相关会议论文 前1条

1 王宾;晋卫;郭伟;吕效平;;聚偏氟乙烯超滤膜超声辅助清洗及强化膜过滤[A];第三届全国化学工程与生物化工年会论文摘要集（上）[C];2006年

相关硕士学位论文 前6条

1 周钱华;热致相分离法制备聚偏氟乙烯中空纤维膜[D];北京工业大学;2015年

2 沈伟坚;聚偏氟乙烯(PVDF)超滤膜的制备与亲水性能的改善[D];浙江理工大学;2016年

3 袁健思;改性聚偏氟乙烯分离膜的制备和性能研究[D];东华大学;2017年

4 吕亚文;聚偏氟乙烯超滤膜改性及其抗污染性能的研究[D];北京工业大学;2001年

5 李欣;聚偏氟乙烯导热性能改性研究[D];天津大学;2013年

6 何静;聚偏氟乙烯荷电超滤膜的制备及性能研究[D];东北林业大学;2014年

本文编号：2051143