偏高岭土对SHCC力学性能的影响研究

发布时间：2018-06-25 04:21

  本文选题：偏高岭土 + SHCC　； 参考：《新型建筑材料》2017年10期

【摘要】：用偏高岭土(MK)取代0、5%、10%、15%水泥的配制应变硬化水泥基复合材料(SHCC),以研究MK对SHCC基本力学性能的影响。结果表明,MK作为掺合料能使SHCC的初裂强度、极限拉伸强度、极限拉伸应变、弹性模量和抗压强度等有不同程度的提高,较佳的MK掺量为10%。掺入适量的MK能改善SHCC的多缝开裂特性,细裂纹(宽度为几十微米)数量增加,裂纹平均宽度降低。MK的掺入还能改善PVA纤维与水泥基体的界面粘结性能,界面粘结强度得到提高。
[Abstract]:In order to study the effect of MK on the basic mechanical properties of SHCC, strain hardening cement-based composite (SHCC) was replaced by metakaolin (MK). The results show that the initial crack strength, ultimate tensile strain, elastic modulus and compressive strength of SHCC can be improved by using MK as admixture, and the better addition of MK is 10%. The addition of proper amount of MK can improve the multi-crack cracking characteristics of SHCC. The number of fine cracks (width is several tens microns) and the average crack width decrease. The interfacial bond between PVA fiber and cement base can also be improved by the addition of MK. The bond strength of the interface is improved.
【作者单位】： 武汉理工大学理学院工程结构与力学系;武汉理工大学硅酸盐建筑材料国家重点实验室;
【基金】：湖北省自然科学基金项目(2014CFB866)
【分类号】：TU528

【相似文献】

相关期刊论文 前10条

1 王立久,李明,王宝民;偏高岭土的研究现状及展望[J];建材技术与应用;2003年01期

2 王智宇;;偏高岭土的制备及其在混凝土中的应用[J];建材技术与应用;2006年05期

3 李明玲;李宏林;高晓宝;高华敏;;土聚水泥用高活性偏高岭土的制备[J];巢湖学院学报;2009年03期

4 徐洪国;水中和;章瑞;陈伟;曾俊杰;;偏高岭土对水泥石热膨胀性能的影响[J];硅酸盐通报;2011年02期

5 杨凤玲;嵇银行;李玉寿;阎晓波;;偏高岭土对混凝土性能影响研究[J];混凝土与水泥制品;2011年05期

6 栾进华;汪洋;王伟;杨洪永;;偏高岭土活性快速测试方法研究[J];矿业工程;2011年04期

7 孙长军;马军涛;水中和;李远;;偏高岭土基改性剂在海工混凝土中的应用研究[J];混凝土与水泥制品;2013年03期

8 储诚富;李小春;邓永锋;唐俊玮;;偏高岭土对水泥改性海相软土力学性能的影响[J];岩土工程学报;2013年S1期

9 赵山泉;微波处理对偏高岭土的作用[J];国外建材科技;1996年01期

10 孙彤;;高活性偏高岭土制备最佳工艺参数的研究[J];中国水泥;2013年12期

相关会议论文 前1条

1 杜小满;刘钦甫;邢楠;;朔州煤系高岭岩制备偏高岭土用于混凝土掺合料研究[A];中国矿物岩石地球化学学会第13届学术年会论文集[C];2011年

，

本文编号：2064545