钢渣有价组分的分部高附加值利用

发布时间：2018-07-01 10:31

本文选题：转炉钢渣 + 综合利用　；参考：《过程工程学报》2017年05期

【摘要】：采用选择性碳热还原方法高附加值利用转炉钢渣中有价组分,实验考察了还原温度和时间对转炉钢渣中主要有价元素Fe,P,Mn,Cr等的还原行为及析出多元铁合金(目标相)成分的影响,通过磨矿、磁选分离得到目标相和余渣,以目标相为主要原料合成锂离子电池正极材料掺杂型磷酸铁锂.结果表明,产物0.1C下首次放电容量达159.58 mA×h/g,倍率循环性能良好;余渣主要成分为Ca(OH)_2,2CaO·SiO_2和3CaO·SiO_2,平均粒径约2.5mm且分布均匀,资源特性和利用价值明显提升.
[Abstract]:The effect of reduction temperature and time on the reduction behavior and precipitation of multicomponent ferroalloy (target phase) in converter slag were investigated by the method of selective carbothermal reduction with high added value. The target phase and residue were separated by grinding and magnetic separation. The cathode material of lithium ion battery was synthesized with the target phase as the main raw material. The results show that the initial discharge capacity of the product reaches 159.58 Ma 脳 h / g at 0.1C, and the cycling performance of the ratio is good, and the main components of the residue are Ca (OH) 2CaO SiOStuby 2 and 3CaO-SiOSP 2, the average particle size is about 2.5mm and the distribution is uniform, and the resource characteristics and utilization value are obviously improved.
【作者单位】：安徽工业大学冶金减排与资源综合利用教育部重点实验室;安徽工业大学冶金工程与资源综合利用安徽省重点实验室;
【基金】：安徽省自然科学基金资助项目(编号:1508085ME69) 国家自然科学基金委员会-宝钢集团有限公司钢铁联合研究基金资助项目(编号:U1660105;U1660106) 安徽省冶金固废材料化利用新技术创新团队资助项目
【分类号】：TQ131.11;X757

【相似文献】