钢-PVA混杂纤维混凝土抗冲击性能研究

发布时间：2018-07-08 12:35

  本文选题：钢-PVA混杂纤维 + 混凝土　； 参考：《混凝土》2017年12期

【摘要】：为研究钢纤维与PVA纤维掺量对混凝土抗冲击性能的影响,对两种纤维不同掺量的混杂纤维混凝土进行落锤冲击试验,并设计素混凝土作为对照试验。试验结果表明,单掺纤维混凝土中,钢纤维较PVA纤维对混凝土抗冲击性能提升要大,单掺2%钢纤维时强度最大。加入PVA纤维使其强度和刚度得到再次的提升,其中2%钢纤维、0.1%PVA纤维掺量的增强效果最为显著,屈服载荷较素混凝土得到30%左右的提升,并通过不同冲击能量试验进行了验证。
[Abstract]:In order to study the effect of the content of steel fiber and PVA fiber on the impact resistance of concrete, a drop hammer impact test was carried out on two kinds of hybrid fiber concrete with different fiber content, and the plain concrete was designed as a control test. The test results show that the impact resistance of concrete with steel fiber is higher than that of PVA fiber, and the strength of concrete with 2% steel fiber is the highest. The strength and stiffness of PVA fiber were enhanced again, and the reinforcement effect of 2% steel fiber 0.1% PVA fiber was the most remarkable, and the yield load was about 30% higher than that of plain concrete, which was verified by different impact energy tests.
【作者单位】： 空军勤务学院机场工程与保障系;
【基金】：国家自然科学基金项目(51478462,51508565)
【分类号】：TU528.572

【相似文献】

相关期刊论文 前10条

1 郭靓;;浅谈混杂纤维混凝土的增强机理[J];科技信息;2011年03期

2 张冲;宁博;;混杂纤维混凝土地铁管片数值模拟研究[J];混凝土与水泥制品;2012年10期

3 方和江;李新;;混杂纤维混凝土疲劳试验研究[J];建材世界;2010年06期

4 王量;鞠丽艳;胡春花;;混杂纤维高性能混凝土配合比优化设计[J];城市道桥与防洪;2006年04期

5 宁博;欧阳东;易宁;鲁刘磊;易承波;潘攀;吴亭亭;;混杂纤维混凝土在地铁管片中的应用[J];混凝土与水泥制品;2011年01期

6 王海超;刘校源;;较高韧性混杂纤维混凝土弯曲抗拉性能试验研究[J];混凝土与水泥制品;2011年04期

7 李永鹏;嵇绍华;何锐;陈拴发;;细集料对混杂纤维混凝土性能的影响[J];混凝土;2013年06期

8 夏冬桃;周博儒;刘向坤;杨应平;;低掺量三元混杂纤维混凝土轴拉性能试验[J];华中科技大学学报(自然科学版);2013年11期

9 李习波;焦楚杰;高俊岳;王龙;艾武波;;混杂纤维混凝土研究进展[J];低温建筑技术;2014年01期

10 陈家来;;混杂纤维混凝土抗弯冲击性能[J];科技促进发展;2010年S1期

相关会议论文 前3条

1 朋改非;康义荣;;高温对混杂纤维活性粉末混凝土力学性能的影响[A];2013年混凝土与水泥制品学术讨论会论文集[C];2013年

2 燕兰;邢永明;郝，

本文编号：2107450