干燥和浸水环境下基于无损检测方法的镁水泥砼最佳配合比研究
发布时间：2018-08-23 21:09
【摘要】：针对西部盐湖地区耐腐蚀混凝土的需求和结合当地实际情况,设计了在干燥环境下与浸水环境下,通过对相对动弹性模量、相对质量、综合评价参数及扫描电子显微镜试验的研究来判断镁水泥混凝土的性能。通过研究发现:采用无损检测试验方法进行为期一年的试验后发现,镁水泥混凝土的6种配合比中性能最好的配合比是配合比2,而它所用材料的比例为:水∶MgO∶MgCl_2∶石子∶砂子∶磷肥∶减水剂=1∶2.87∶1.09∶8.57∶4.61∶0.07∶0.12。
[Abstract]:According to the demand of corrosion-resistant concrete in the western salt lake area and the local actual situation, the relative dynamic modulus of elasticity and the relative mass of concrete are designed under the dry environment and the immersion environment. Comprehensive evaluation of the parameters and scanning electron microscope test to judge the performance of magnesium cement concrete. After a year of nondestructive testing, it was found that, The best mixture ratio of the six kinds of mg cement concrete is mixture ratio 2, and the proportion of the materials used is: water: MgO: MgCl 2: stone: sand: phosphate fertilizer: water reducer 1: 2. 87: 1.09: 8.57: 4.61: 0. 07: 0. 12.
【作者单位】： 兰州理工大学甘肃省土木工程防灾减灾重点实验室;西部土木工程防灾减灾教育部工程研究中心;郑州工业应用技术学院建筑工程学院;
【基金】：国家自然科学基金项目(51468039) 中国科学院盐湖资源与化学重点实验室开放基金资助(KLSLRC-KF-13-HX-8)
【分类号】：TU528
本文编号：2199923
[Abstract]:According to the demand of corrosion-resistant concrete in the western salt lake area and the local actual situation, the relative dynamic modulus of elasticity and the relative mass of concrete are designed under the dry environment and the immersion environment. Comprehensive evaluation of the parameters and scanning electron microscope test to judge the performance of magnesium cement concrete. After a year of nondestructive testing, it was found that, The best mixture ratio of the six kinds of mg cement concrete is mixture ratio 2, and the proportion of the materials used is: water: MgO: MgCl 2: stone: sand: phosphate fertilizer: water reducer 1: 2. 87: 1.09: 8.57: 4.61: 0. 07: 0. 12.
【作者单位】： 兰州理工大学甘肃省土木工程防灾减灾重点实验室;西部土木工程防灾减灾教育部工程研究中心;郑州工业应用技术学院建筑工程学院;
【基金】：国家自然科学基金项目(51468039) 中国科学院盐湖资源与化学重点实验室开放基金资助(KLSLRC-KF-13-HX-8)
【分类号】：TU528
【相似文献】
相关期刊论文 前6条
1 刘曙光;王志伟;闫长旺;张菊;闫敏;;基于灰色理论的PVA-FRCC抗盐冻性能分析[J];建筑科学与工程学报;2014年01期
2 刘曙光;王志伟;张菊;闫长旺;白建文;;基于灰色理论的PVA-FRCC抗冻性寿命预测[J];混凝土与水泥制品;2013年08期
3 张云清;余红发;王甲春;;气泡特征对混凝土抗盐冻性能的影响[J];建筑科学与工程学报;2011年03期
4 汪廷秀;高建明;丁平华;陈吓敏;刘艳玲;;干湿交替作用下混凝土抗硫酸盐侵蚀性能研究[J];混凝土与水泥制品;2011年02期
5 霍俊芳;于乃领;王婷;;大掺量粉煤灰混凝土冻融损伤模型及剩余寿命预测[J];混凝土;2013年12期
6 ;[J];;年期
，本文编号：2199923
本文链接：https://www.wllwen.com/kejilunwen/huaxuehuagong/2199923.html