双掺聚丙烯纤维与聚酯纤维混凝土抗冲击性能试验研究

发布时间：2018-09-14 11:28

【摘要】：利用压汞法(MIP)测试了不同锂渣掺量的C30、C60混凝土的孔结构参数,计算了被测混凝土的孔体积分形维数、孔轴线分形维数,并研究了混凝土气体渗透系数、锂渣掺量与孔体积分形维数、孔轴线分形维数之间的关系。结果表明,混凝土的气体渗透系数与孔体积分形维数相关性高;C60混凝土在锂渣掺量为10%时,孔体积分形维数和孔轴线分形维数最大;随着锂渣掺量的提高,C30混凝土孔体积分形维数和孔轴线分形维数呈降低的趋势。
[Abstract]:The pore structure parameters of C _ (30) C _ (60) concrete with different lithium slag content were measured by (MIP) method. The pore volume fractal dimension and pore axis fractal dimension of concrete were calculated, and the gas permeability coefficient of concrete was studied. The relationship between the content of lithium slag and the fractal dimension of pore volume and pore axis. The results show that the correlation between the gas permeability coefficient and the fractal dimension of pore volume is high. When the content of lithium slag is 10, the fractal dimension of pore volume and the fractal dimension of pore axis are the largest. With the increase of the content of lithium slag, the fractal dimension of pore volume and the fractal dimension of pore axis of C30 concrete decrease.
【作者单位】： 空军勤务学院机场工程与保障系;
【基金】：国家自然科学基金项目(51478462,51508565)
【分类号】：TU528

【相似文献】

相关期刊论文 前7条

1 王玉鹏;;聚丙烯纤维混凝土抗冲击性能研究[J];江西建材;2014年12期

2 万文乾;龙源;纪冲;朱燕燕;;钢纤维混凝土抗冲击性能的数值模拟研究[J];南京理工大学学报(自然科学版);2007年01期

3 王伯昕;黄承逵;;大直径合成纤维增强混凝土抗冲击性能的研究[J];建筑材料学报;2006年05期

4 朱洪波;李晨;闫美珠;吴梦雪;;水泥-聚苯乙烯轻质材料的制备及抗冲击性[J];同济大学学报(自然科学版);2014年05期

5 ;信息与咨询[J];中国建材;1985年09期

6 李武学;张宝明;;改性聚丙烯纤维对混凝土抗冲击性能的影响机理与试验研究[J];天津科技;2011年03期

7 ;[J];;年期

相关硕士学位论文 前2条

1 刘臣;合成纤维增强混凝土抗冲击性能试验研究[D];广西大学;2012年

2 李佳宇;高硬度高韧性特种玻璃的研究[D];长春理工大学;2014年

，

本文编号：2242578