低强度自密实再生大骨料混凝土配制试验研究

发布时间：2018-10-08 13:15

【摘要】：通过自密实再生大骨料混凝土的配制试验,研究了水胶比、高效减水剂对自密实再生混凝土强度及和易性的影响规律。结果表明:当水胶比W/B=0.55,高效减水剂掺量为胶凝材料的0.6%时,混凝土拌合物整体和易性良好,且无泌水现象发生,其抗压强度为18.1~20.5 Mpa。对于低强度混凝土建筑物,其承载力方面可以满足要求,具有一定技术可行性。
[Abstract]:The effects of water-binder ratio and superplasticizer on strength and easiness of self-compacting recycled concrete were studied through the preparation test of self-compacting recycled aggregate concrete. The results show that when the ratio of water to binder is 0.55 and the content of superplasticizer is 0.6, the whole and easiness of concrete mixture is good, and there is no bleeding phenomenon. The compressive strength of concrete is 18.1g 20.5 Mpa.. For low-strength concrete buildings, its bearing capacity can meet the requirements and has certain technical feasibility.
【作者单位】： 河北农业大学城乡建设学院;
【基金】：河北省高等学校科学技术研究项目(ZD2015019) 河北农业大学理工基金(LG20150302) 河北省现代农业产业体系蔬菜产业创新团队建设项目
【分类号】：TU528

【参考文献】

相关期刊论文 前6条

1 王海超;孙利敏;;再生大骨料自密实堆石混凝土力学性能研究[J];混凝土;2013年08期

2 李静;王林富;刘震;姜琳;;再生大骨料影响自密实堆积混凝土力学性能的试验研究[J];科学技术与工程;2010年13期

3 许岳周;石建光;;再生骨料及再生骨料混凝土的性能分析与评价[J];混凝土;2006年07期

4 刘小洁;余志武;;自密实混凝土的研究与应用综述[J];铁道科学与工程学报;2006年02期

5 余志武,潘志宏,谢友均,刘宝举;浅谈自密实高性能混凝土配合比的计算方法[J];混凝土;2004年01期

6 赵筠;自密实混凝土的研究和应用[J];混凝土;2003年06期

【共引文献】

相关期刊论文 前10条

1 王哲波;;C80钢管自密实混凝土工作性试验研究[J];低温建筑技术;2017年07期

2 郭鹏;韦万峰;杨帆;杨晓宇;;再生集料及再生混凝土界面过渡区研究进展[J];硅酸盐通报;2017年07期

3 李雪U，

本文编号：2256888