掺加卤化钠改善金属镁的初始活化性能

发布时间：2017-12-31 03:24

本文关键词：掺加卤化钠改善金属镁的初始活化性能　出处：《功能材料》2016年12期 　论文类型：期刊论文

【摘要】：金属镁用作储氢材料时由于表面存在氧化膜,在首次吸氢反应过程中需要一定的时间活化,即存在着吸氢孕育期。为了消除这个孕育期,本文利用高能机械球磨法在金属镁中掺杂卤化钠(NaCl和NaBr)。结果表明,加入NaCl、NaBr添加剂后,样品Mg-NaCl和Mg-NaBr在2 000kPa氢气压力下,573和608K时的首次吸氢反应中均没有检测到孕育期的存在,吸氢量分别为5.6和5.0%(质量分数)。虽然利用高能机械球磨法掺杂卤化钠能显著改善金属镁的首次吸氢反应动力学性能,但在调控热力学性能方面没有发挥太大的作用。
[Abstract]:When magnesium is used as a hydrogen storage material, due to the existence of oxide film on the surface, it needs a certain time to activate in the process of the first hydrogen absorption reaction, that is, the incubation period of hydrogen absorption exists, in order to eliminate the incubation period. The high energy mechanical ball milling method was used to doping sodium halide sodium chloride and NaBr1 in magnesium metal. The results showed that the addition of NaCl-nabr additive was carried out. No gestation period was detected in the first hydrogen absorption reaction of samples Mg-NaCl and Mg-NaBr at 2 000 KPA hydrogen pressure at 573 and 608 K. The hydrogen absorption amounts were 5.6 and 5.0 (mass fraction) respectively. Although doping sodium halide by high-energy mechanical ball milling method can significantly improve the kinetic properties of the first hydrogen absorption reaction of magnesium metal. However, it does not play a significant role in regulating thermodynamic properties.
【作者单位】：桂林电子科技大学材料科学与工程学院广西信息材料重点实验室广西新能源材料结构与性能协同创新中心;加拿大魁北克大学三河城分校氢能研究所;
【基金】：国家自然科学基金资助项目(51361006,51401059,51461010,51361005,51371060,51461011,U1501242) 广西自然科学基金资助项目(2014GXNSFAA118043,2014GXNSFAA118333) 桂林电子科技大学研究生教育创新计划资助项目(2016YJCX22)
【分类号】：TG146.22
【正文快照】： 2.加拿大魁北克大学三河城分校氢能研究所,魁北克三河市G9A5H7)0引言对于氢气燃料电池来说,在适宜的条件下可以可逆吸放氢的储氢材料是不可或缺的[1]。固态储氢材料由于具有氢含量高和安全性好等优点,一直是研究的热点方向[2]。目前,在众多的固态储氢材料中,金属镁具有高的储