光纤激光焊接铝合金离焦量对焊缝成形的影响

发布时间：2018-01-02 23:22

本文关键词：光纤激光焊接铝合金离焦量对焊缝成形的影响　出处：《激光与光电子学进展》2016年12期 　论文类型：期刊论文

【摘要】：采用高功率光纤激光对3mm厚铝合金进行焊接实验,系统研究了离焦量对焊缝熔池形貌、熔深、熔宽、底部驼峰及深宽比、宽度比例系数的影响。结果表明,随着离焦量的增加,焊接模式由深熔焊转变为热导焊,熔宽变化不明显,底部驼峰高度和宽度比例系数降低;用高功率光纤激光焊接时,通过减小负离焦量或改变为正离焦的方式能降低焊缝塌陷程度与底部驼峰高度;用较低功率光纤激光焊接时,通过增大负离焦量或减小正离焦量的方式能增大背面熔宽。
[Abstract]:The use of high power fiber laser welding of 3mm thick Aluminum Alloy experiment system of defocus on the weld pool shape, weld penetration, weld width, bottom hump and depth to width ratio, width ratio. The results show that with the increase of defocusing amount, welding mode transition by welding for heat conduction welding, the weld width did not change significantly, reduce the hump height and width ratio; for high power fiber laser welding, by reducing the negative defocus or change positive defocus mode can reduce weld collapse degree and bottom hump height; low power fiber laser welding, by increasing the negative defocus or reduce the positive defocus mode can increase the back weld width.

【作者单位】：华中科技大学激光加工国家工程研究中心;温州大学浙江省激光加工机器人重点实验室;温州职业技术学院温州激光应用工程技术研究中心;
【基金】：国家自然科学基金(51605338) 浙江省教育厅资助项目(Y201533195) 温州市科技计划(J20140026,2014F004,G20140050,G20150003) 温州市重点科技创新团队项目(C20150006)
【分类号】：TG456.7
【正文快照】： 1引言 2124铝合金为Al-Cu系硬铝合金,具有较强的断裂韧性、抗疲劳与应力腐蚀等优良综合性能,已成为航空航天工业的主要结构材料。用于铝合金焊接的传统方法主要为钨极稀有气体保护焊(TIG)与熔化极稀有气体保护焊(MIG),但传统TIG、MIG焊接方法的热源能量密度低、热输入量大,