Q235低碳钢的点腐蚀声发射检测实验研究

发布时间：2018-01-11 03:16

  本文关键词：Q235低碳钢的点腐蚀声发射检测实验研究　出处：《中国特种设备安全》2016年12期 　论文类型：期刊论文

  更多相关文章： 低碳钢 点腐蚀 声发射

【摘要】：本文搭建了基于美国物理声学公司生产的微型SAMOS声发射监测系统的实验平台,对压力容器常用金属材料Q235低碳钢点腐蚀过程中产生的声发射信号进行了实验测量。通过研究,对金属材料点腐蚀过程的声发射检测及信号处理方法有了较为全面的认识,为声发射技术在腐蚀监测方面的进一步研究及应用提供了有价值的参考。
[Abstract]:In this paper, the experimental platform of the micro SAMOS acoustic emission monitoring system based on the American physical acoustics company is built. The acoustic emission (AE) signals produced during the pitting corrosion of Q235 low carbon steel, a metal material commonly used in pressure vessels, were measured experimentally. The methods of acoustic emission detection and signal processing in the process of spot corrosion of metal materials have been fully understood, which provides a valuable reference for the further study and application of acoustic emission technology in corrosion monitoring.
【作者单位】： 西安特种设备检验检测院;西安交通大学;
【分类号】：TG142.15;TG115.28
【正文快照】： 金属腐蚀是指金属在环境或介质的作用下所引起的破坏或变质。对于在用的压力容器或压力管道来说,腐蚀是造成设备损坏、构件失效的重要原因。对于低碳钢来说,点蚀所造成的损失是很大的[1]。由于点蚀是一种高度集中的局部腐蚀形态,当低碳钢表面出现点蚀时,蚀坑会随着时间的推移

【相似文献】

相关期刊论文 前10条

1 陈学兵;;露点腐蚀及防护[J];石油化工腐蚀与防护;1988年04期

2 许适群;关于露点腐蚀及用钢的综述[J];石油化工腐蚀与防护;2000年01期

3 许适群;关于露点腐蚀及用钢的综述(二)[J];石油化工腐蚀与防护;2000年03期

4 林昌健;田昭武;;不锈钢点腐蚀发生的早期过程 Ⅰ.扫描微参比电极法研究[J];物理化学学报;1987年05期

5 顾福元;;醋酸乙酯管道点腐蚀失效分析[J];上海化工;2010年10期

6 李强;陈谦;;浅谈催化裂化再生系统低温露点腐蚀成因及解决对策[J];通用机械;2007年03期

7 赵克勤;朱洪洲;郭永;;新氢炉管露点腐蚀的初步分析[J];炼油设备设计;1984年05期

8 王杰;刘贺;刘丽;张兴铎;;308L不锈钢堆焊试板点腐蚀原因分析[J];大型铸锻件;2011年06期

9 林昌健,谢兆雄,田昭武;不锈钢点腐蚀发生的早期过程Ⅱ.电化学扫描隧道显微研究[J];腐蚀科学与防护技术;1997年04期

10 张磊;热媒炉的露点腐蚀与防护[J];石油化工腐蚀与防护;2003年01期

相关会议论文 前1条

1 徐强;万正权;;含坑点腐蚀的深海耐压球壳有限元分析[A];中国钢结构协会海洋钢结构分会2010年学术会议暨第六届理事会第三次会议论文集[C];2010年

相关硕士学位论文 前1条

1 刘国卿;常顶系统低温部位露点腐蚀电化学实验研究[D];西安石油大学;2012年

，

本文编号：1407907