搅拌摩擦加工制备镁基铝覆层材料的组织与性能

发布时间：2018-01-17 16:25

本文关键词：搅拌摩擦加工制备镁基铝覆层材料的组织与性能　出处：《焊接学报》2017年01期 　论文类型：期刊论文

【摘要】：在采用多道次搅拌摩擦加工成功地在镁合金表面覆合一层铝层的基础上,利用光学显微镜、透射电子显微镜、扫描电子显微镜、能谱分析和电子万能材料试验机对界面组织、元素成分分布、界面结合力和断口形貌进行了分析,并分析了不同焊接速度对重叠区界面组织和性能的影响规律.结果表明,界面由N道次区、重叠区和N+1道次区组成,重叠区界面过渡层的厚度随着焊接速度的降低而增加.其过渡层由Al+Al3Mg2相和Mg+Al12Mg17相组成.重叠区界面的剪切力随着速度的降低而增加,断裂方式为塑性断裂.
[Abstract]:On the basis of successfully covering a layer of aluminum layer on the surface of magnesium alloy by multi-pass friction stir processing, optical microscope, transmission electron microscope and scanning electron microscope were used. The interfacial structure, element composition distribution, interfacial adhesion and fracture morphology were analyzed by energy spectrum analysis and electronic universal material testing machine. The effects of different welding speeds on the microstructure and properties of the superimposed zone are analyzed. The results show that the interface is composed of N pass zone, overlapping zone and N 1 pass subregion. The thickness of interfacial transition layer increases with the decrease of welding speed. The transition layer is composed of Al Al3Mg2 phase and mg. The shear force of the superimposed interface increases with the decrease of the velocity. The fracture mode is plastic fracture.
【作者单位】：大连交通大学材料科学与工程学院;安阳工学院机械工程学院;
【基金】：教育部高等学校博士学科点专项科研基金(20132124120003) 辽宁省教育厅科学研究一般项目(L2014185)
【分类号】：TG453.9
【正文快照】： 0序言镁合金因具有比强度高、低密度、高刚性等特点,而作为一种最具理想的轻量化材料在交通运输工业领域中得到广泛的应用[1].但是由于镁的化学性质较为活泼,且在镁表面形成的氢氧化镁氧化膜疏松多孔,保护基体的能力较弱,尤其是在含有Cl-,Br-,SO2-4的溶液中更容易腐蚀,因而镁

【相似文献】