文献名称：离心铸造高速钢轧辊铸造缺陷形成与控制技术研究

    前言：采用离心铸造方法制造高速钢轧辊工艺简单,操作方便,但易出现偏析、裂纹、气孔、缩孔及夹杂等缺陷,影响轧辊的力学性能和使用性能。采用稀土—钛复合变质处理改善合金的组织和性能,同时改进离心铸造工艺参数可以消除高速钢轧辊铸造缺陷,提高力学性能,改善使用效果。
    Centrifugal casting technology has such characteristics as simple process and easy operation to manufacture high speed steel roll. It is also easy to produce many casting defects such as segregation, crack, air hole, shrinkage and inclusion etc., which decreases the mechanical performances and service properties. Adopting modification process with rare earth (RE) and titanium, the microstructure and performance are obviously improved, and improving centrifugal casting parameter at the same time, the casting...

文献名称 离心铸造高速钢轧辊铸造缺陷形成与控制技术研究

Article Name
英文(英语)翻译 Study on Defect Formation and Controlling of Centrifugal Casting High Speed Steel Roll;

作者 符寒光; 邢建东;

Author FU Han-guang~1;XING Jian-dong~2 （1. Department of Mechanical Engineering;Tsinghua University;Beijing 100084;2. School of Materials Science & Engineering;Xi'an Jiaotong University;Xi'an 710049;China）;

作者单位
Author Agencies 清华大学机械工程系; 西安交通大学材料科学与工程学院 北京; 陕西西安;

文献出处
Article From 中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度

关键词 高速钢轧辊; 离心铸造; 铸造缺陷;

Keywords High-speed steel roll;Centrifugal casting;Casting defect;

高碳高速钢轧辊中合金元素的作用及成分设计
钛变质高速钢轧辊的组织和性能
高速钢轧辊热处理工艺参数的预测
热轧粗轧用半高速钢轧辊材料中碳化物的氧化行为
高速钢轧辊材料的研究进展
珠钢热轧机高速钢轧辊应用技术开发
神经网络的BP算法研究高速钢轧辊的热处理工艺
棒线材用小离心高速钢轧辊铸造工艺研究
铸造高速钢轧辊在热连轧机组上的应用研究
离心机双头浇注双金属复合铸管

  本文关键词：离心铸造高速钢轧辊铸造缺陷形成与控制技术研究，由笔耕文化传播整理发布。