氚老化对海绵钯吸、放氕氘热力学性质的影响

发布时间：2018-01-22 00:17

  本文关键词： 海绵钯 氚老化 热力学性质　出处：《稀有金属材料与工程》2017年10期 　论文类型：期刊论文

【摘要】：钯是氚处理工艺中的关键功能材料,氚衰变及其产生的氦会引起钯的贮氢性能下降。对室温下贮氚老化1.6年的海绵钯进行了预处理,采用变温法获得了老化钯吸、放氕和氘的PCT曲线,作为对比,同时给出了新鲜钯的实验结果。在此基础上,进行了氚老化钯吸、放氕和氘热力学性质分析。结果显示,氚老化会导致钯氢体系的α相右移、坪台压降低、坪台区变窄,且老化效应对钯氢体系的滞后效应、焓变及熵变产生影响。
[Abstract]:Palladium is a key functional material in tritium treatment process. Tritium decay and the helium produced will cause the degradation of hydrogen storage performance of palladium. The sponge palladium aged 1.6 years after tritium aging at room temperature was pretreated. The PCT curves of aging palladium absorption, protium and deuterium were obtained by variable temperature method. The experimental results of fresh palladium were also given. On the basis of this, tritium aging palladium absorption was carried out. The thermodynamic properties of Protium and deuterium are analyzed. The results show that tritium aging will lead to the right shift of 伪 phase, the decrease of plateau pressure and the narrowing of plateau area, and the hysteresis effect of aging effect on palladium hydrogen system. Enthalpy change and entropy change influence.
【作者单位】： 中国工程物理研究院;
【基金】：国家自然科学基金(21573200)
【分类号】：TG146.36
【正文快照】： 作为潜在的核反应能源,氘氚聚变释放的能量比同等质量裂变能大得多,并且燃料来源充足,因此在国际热核聚变实验堆(ITER)计划中核聚变被认为是未来能源之一。聚变反应的燃料主要是氘、氚,当燃料中存在氕时,对氘、氘反应和氘、氚反应会产生阻碍。为了使燃料气中的氕含量尽可能少,

【相似文献】

相关期刊论文 前10条

1 窦士学;;硅酸盐熔体的结构及热力学性质[J];钢铁;1981年05期

2 朱锡熊,田德诚;铟-锑系统热力学性质的计算[J];金属学报;1965年01期

3 颜坤志;高温空气的热力学性质[J];力学进展;1985年04期

4 孙运涌;杜挺;;铝-铈-铅、铝-铈-锡溶液体系的热力学性质[J];中国有色金属学报;1993年03期

5 李瑞青,乔芝郁,段淑贞,周国治;常用二元熔盐氯化物相图及其热力学性质的最优化[J];北京钢铁学院学报;1987年03期

6 丘克强,戴永年,陈枫;铅锑二元系热力学性质的研究[J];有色金属;1990年03期

7 杜挺;稀土元素在铁基、镍基溶液中的热力学性质、相平衡及其作用机理的研究[J];物理;1990年01期

8 陈启元，曾文明，张平民，顾松青，杨冠群，周辉放，，尹中林;几种铝化合物的热力学性质[J];金属学报;1996年01期

9 唐恺;韩恒馀;徐建伦;;Si-Al-Ba三元亲热力学性质预测[J];浙江冶金;1994年03期

10 彭瑞伍,闻诗祖;SnCl_2-KCl熔体的热力学性质[J];金属学报;1966年02期

相关硕士学位论文 前1条

1 胡文成;镁合金中典型Laves相结构、电子和热力学性质的第一性原理研究[D];南昌大学;2015年

本文编号：1452997