合金元素对镍基粉末高温合金FGH97的强化作用

发布时间：2018-02-12 00:13

  本文关键词： FGH 合金化 抗拉强度 固溶强化 共格应变强化　出处：《稀有金属材料与工程》2017年06期 　论文类型：期刊论文

【摘要】：运用高温合金强化机理,在FGH97合金标准成分的基础上,调整Co、Cr、Mo、W 4种合金化元素的含量,设计制备了3种合金,以研究合金元素对合金的强化作用。结果表明:调整合金元素含量后,FGH97合金中γ晶格常数获得提高,起到了固溶强化的效果,同时γ/γ′相错配度绝对值的提高增强了共格应变强化的效果;调整合金元素含量对显微组织、γ′相和碳化物等相的析出没有明显影响,没有增强晶界强化和沉淀强化的效果;固溶强化对强度增量的贡献值最高。
[Abstract]:The use of high temperature alloy strengthening mechanism, based on the standard components of FGH97 alloy, Cr, adjusted Co, Mo, W content of 4 kinds of alloying elements, 3 kinds of alloys were prepared. In order to study the strengthening effect of alloy elements on the alloy. The results show that the adjustment of the content of alloying elements, FGH97 gamma lattice gold in improving the solution strengthening effect, at the same time gamma / gamma prime phase error absolute value of enhance the coherent strain strengthening effect; adjusting elements in alloy on microstructure, precipitation of gamma prime phase and carbide phase had no obvious effect, no enhancement of grain boundary strengthening and precipitation strengthening effect solid solution strengthening; on the strength of the incremental contribution of the highest value.

【作者单位】： 钢铁研究总院;高温合金新材料北京市重点实验室;
【基金】：国家国际科技合作专项(2014DFR50330)
【分类号】：TG132.3

【参考文献】

相关期刊论文 前5条

1 张义文;刘建涛;;粉末高温合金研究进展[J];中国材料进展;2013年01期

2 张义文;王福明;胡本芙;;Hf含量对FGH97合金γ/γ′晶格错配度的影响[J];稀有金属材料与工程;2012年06期

3 刘建涛;张义文;陶宇;张莹;张国星;迟悦;;FGH97合金的显微组织[J];材料热处理学报;2011年03期

4 王璞;董建新;张义文;谢锡善;;热处理对FGH96粉末高温合金裂纹扩展速率的影响[J];稀有金属材料与工程;2010年01期

5 田素贵;夏丹;李唐;孟凡来;王明罡;于兴福;;W含量及组织状态对镍基高温合金晶格常数及错配度的影响[J];航空材料学报;2008年04期

【共引文献】

相关期刊论文 前7条

1 蔡文华;杨西荣;刘晓燕;罗雷;陈小龙;;工业纯锆的室温压缩变形行为[J];金属热处理;2017年06期

2 郭亚昆;帅茂兵;邹东利;肖大武;何立峰;;应变水平对锆合金动载下塑性变形机制的影响[J];稀有金属材料与工程;2017年06期

3 胡时胜;王礼立;宋力;张磊;;Hopkinson压杆技术在中国的发展回顾[J];爆炸与冲击;2014年06期

4 李建辉;毛磊;张福成;王琦;国栋;马静;李强;;铝含量和退火温度对锆铝合金相组成和力学性能的影响[J];稀有金属材料与工程;2014年09期

5 邹东利;栾佰峰;肖东平;;应变速率对锆合金塑性变形机制的影响[J];稀有金属材料与工程;2014年08期

6 迟煜，

本文编号：1504339