DP-TIG焊接方法工艺研究

发布时间：2018-02-25 08:12

  本文关键词： 深熔氩弧焊 工艺试验 低碳钢 不锈钢　出处：《焊接》2017年03期 　论文类型：期刊论文

【摘要】：深熔氩弧焊接方法(DP-TIG,Deep Penetration Tungsten Inert Gas Welding)是通过对钨极的高效冷却,压缩电弧,获得能量密度大、挺度高的电弧,可以实现穿孔形式的焊接,达到增大焊接熔深的目的。试验针对低碳钢和不锈钢两种焊接母材,通过调整相关的工艺参数,实现稳定的穿孔型焊接,最终实现低碳钢10 mm以下板厚,不开坡口平板对接焊的单面焊双面成形及不锈钢12 mm以下板厚,不开破口平板对接焊的单面焊双面成形焊接工艺,极大地提高TIG焊的焊接效率。
[Abstract]:Deep penetration argon arc welding method: DP-TIGN Deep Penetration Tungsten Inert Gas Weldinging is a kind of arc with high energy density and high stiffness, which can be used to weld through the high efficiency cooling of tungsten electrode and compression arc. Aiming at two kinds of welding base metal, low carbon steel and stainless steel, through adjusting the relevant process parameters, the stable perforated welding is realized, and the thickness of low carbon steel less than 10 mm is finally realized. The single side welding and double side forming of flat butt welding without opening groove and the thickness of stainless steel less than 12 mm, and the single side welding and double side forming of non opening flat plate butt welding, greatly improve the welding efficiency of TIG welding.
【作者单位】： 唐山开元焊接自动化技术研究所;
【分类号】：TG444.74

【相似文献】

相关期刊论文 前10条

1 ;48/2支国毛变斜花呢工艺试验小结[J];毛纺科技;1977年06期

2 夏志仁;;保温瓶吹泡机“合二为一”的工艺试验[J];玻璃与搪瓷;2008年02期

3 沈祖珉;醋酯人丝产品的工艺试验[J];丝绸;1990年06期

4 戴军;;杭氧工艺所1995年工艺试验成果介绍[J];杭氧科技;1996年01期

5 马静芬,须雅萍;取消6110连杆正火工艺试验[J];金属热处理;1998年01期

6 郑红平;低温练工艺试验和实践[J];丝绸;2001年06期

7 李文超,王俭,朱元凯,王玉集,公花秀,杨文礼,于殿宝;稀土在导电铜中应用工艺试验分析[J];稀土;1992年03期

8 高一新,姜辉;利用计算机进行气体补碳的工艺试验[J];铸锻热;1996年01期

9 毛麒瑞;一种无氰镀银工艺试验成功[J];珠宝科技;1999年04期

10 田文明;;以钻代铰工艺试验与实现[J];机械制造;2008年05期

相关会议论文 前2条

1 张舒;;工艺技术开发工作的浅见[A];铁路货车制造工艺学术研讨会论文集[C];2007年

2 庞玉申;邱宪增;;小规格冲模机械强度的工艺试验与检测分析[A];第三届“兴业杯”中国制药装备论文集[C];2007年

相关硕士学位论文 前1条

1 龚欢;40Cr钢磨削强化工艺试验与温度场仿真研究[D];南京航空航天大学;2007年

，

本文编号：1533634