形变温度对Ti-Ni合金超弹性弹簧形变行为的影响

发布时间：2018-03-03 04:05

  本文选题：Ti-Ni.合金　切入点：弹簧　出处：《热加工工艺》2016年20期 　论文类型：期刊论文

【摘要】：采用拉伸试验和应力应变循环试验研究了形变温度及应力应变循环对Ti-Ni_(50.8)超弹性弹簧形变行为的影响。结果表明:当形变温度在247K以下时Ti-Ni_(50.8)弹簧呈形状记忆性,形变温度在247K以上时呈超弹性特性。623~773K退火态Ti-Ni_(50.8)弹簧室温下可获得良好超弹性。当退火温度超过873K后,超弹性衰减。在应力-应变循环早期,弹簧应变恢复率衰减很快,随循环次数增加,衰减变慢。Ti-Ni_(50.8)弹簧预先应力应变循环训练可增强其变形稳定性。
[Abstract]:The effects of deformation temperature and stress-strain cycle on the deformation behavior of Ti-NiJI (50.8) superelastic spring were studied by means of tensile test and stress-strain cycling test. The results show that the Ti-NiNiLi (50.8)) spring exhibits shape memory when the deformation temperature is below 247K. A good hyperelasticity can be obtained at room temperature when the deformation temperature is above 247K. The strain recovery rate of the spring attenuates rapidly at the early stage of stress-strain cycle when the annealing temperature exceeds 873K. With the increase of cycle times, the attenuation becomes slower. Ti-NiSZ (50.8) spring pre-stress-strain cycle training can enhance its deformation stability.
【作者单位】： 榆林职业技术学院机电工程系;陕西理工学院材料科学与工程系;
【分类号】：TG139.6

【相似文献】

相关期刊论文 前10条

1 李强;朱胜利;崔振铎;杨贤金;;新型无镍β型钛合金超弹性的研究[J];材料热处理学报;2011年12期

2 阚前华;康国政;宋迪;于超;蒋晗;;残余应变对镍钛形状记忆合金超弹性抑制效应的实验研究[J];四川大学学报(工程科学版);2012年S2期

3 ;一种超弹性钛镍丝材处理方法及装置[J];钛工业进展;1999年04期

4 金嘉陵;镍钛合金的超弹性[J];上海钢研;1990年01期

5 黄兵民,蔡伟,赵蔚,赵连城,刘礼华;应力-应变循环对Ti-49.8at%Ni合金非线性超弹性的影响[J];稀有金属;1997年06期

6 于振涛;郑玉峰;周 廉;王本力;牛金龙;皇甫强;张亚锋;;新型Ti-3Zr-2Sn-3Mo-15Nb钛合金的形状记忆和超弹性(英文)[J];稀有金属材料与工程;2008年01期

7 康国政;;超弹性镍钛形状记忆合金循环变形行为的研究进展[J];西南交通大学学报;2011年03期

8 郭锦芳;第二届国际形状记忆和超弹性技术工程、医学应用会议[J];钛工业进展;1997年06期

9 罗洪艳;高，

本文编号：1559442