碳钢表面等离子喷涂NiCrAl涂层的耐蚀性能研究

发布时间：2018-03-04 03:28

  本文选题：等离子喷涂　切入点：Ni　出处：《热加工工艺》2017年22期 　论文类型：期刊论文

【摘要】：采用高温高压及电化学腐蚀实验研究了Q235钢、13Cr以及Q235钢表面沉积Ni Cr Al涂层后的耐CO2腐蚀性能。Ni Cr Al涂层采用等离子喷涂制备。结果表明:Q235钢抗均匀腐蚀和局部腐蚀的能力较差;13Cr抗均匀腐蚀能力良好,但出现明显的点蚀;Ni Cr Al涂层具有良好的抗均匀腐蚀及点蚀能力。Ni Cr Al涂层的通孔结构为腐蚀介质提供了渗入通道,进而腐蚀界面处的Q235钢。
[Abstract]:The corrosion resistance of NiCrAl coating on Q235 steel and Ni-CrAl coating on Q235 steel was studied by high temperature and high pressure and electrochemical corrosion experiments. The results showed that the corrosion resistance of Q235 steel was uniform and local. The ability of corrosion is poor and the uniform corrosion resistance of 13Cr is good. But the obvious pitting corrosion of Ni Cr Al coating has good resistance to uniform corrosion and pitting corrosion. The through pore structure of Ni Cr Al coating provides an infiltration channel for corrosion medium and then corrodes Q235 steel at the interface.
【作者单位】： 西安石油大学材料科学与工程学院;
【基金】：国家自然科学基金资助项目(51605384) 陕西省自然科学基础研究计划项目(2016JQ5077) 陕西省教育厅专项科研计划项目(16JK1597) 西安石油大学《材料科学与工程》省级优势学科资助(YS37020203)
【分类号】：TG174.4

【相似文献】

相关期刊论文 前10条

1 李行志,胡树兵;等离子喷涂的发展及其应用[J];湖北汽车工业学院学报;2004年02期

2 陈丽梅;李强;;等离子喷涂技术现状及发展[J];热处理技术与装备;2006年01期

3 ;武汉材保所：重新启用高能等离子喷涂设备 为建设“两型”社会作贡献[J];表面工程资讯;2008年02期

4 ;等离子喷涂设备简介[J];材料保护;1966年04期

5 ;等离子喷涂[J];机车车辆工艺;1971年05期

6 高奉周;;大功率等离子喷涂枪鉴定会在沈阳举行[J];焊接;1980年06期

7 耿家林;;等离子喷涂修复发动机传动杆[J];航空工艺技术;1981年07期

8 谷式，

本文编号：1563950