高速双螺杆挤出机螺杆轴断裂失效分析

发布时间：2018-03-04 23:37

  本文选题：双螺杆挤出机　切入点：疲劳断裂　出处：《机械工程材料》2017年03期 　论文类型：期刊论文

【摘要】：某双螺杆挤出机的螺杆在运行过程中发生早期断裂,通过断口的宏观观察和扫描电镜观察、化学成分分析、显微组织观察、力学性能测试和有限元模拟,找出了螺杆轴断裂失效的原因。结果表明:螺杆轴发生了扭转疲劳断裂,裂纹起源于齿根,且有多个疲劳源;芯轴的花键齿根部是螺杆轴应力集中的部位;热处理工艺欠佳导致材料内部微孔聚集、组织不均匀,这些因素最终致使螺杆轴发生早期疲劳断裂。
[Abstract]:The screw of a twin-screw extruder had an early fracture in the course of operation. Through macroscopic observation of fracture surface, SEM observation, chemical composition analysis, microstructure observation, mechanical property test and finite element simulation, The results show that torsional fatigue fracture occurs in the screw shaft, the crack originates from the root of the tooth and there are many fatigue sources, and the spline tooth root of the core shaft is the part of the stress concentration of the screw shaft. The poor heat treatment process leads to the accumulation of micropores and uneven microstructure, which leads to the early fatigue fracture of the screw shaft.
【作者单位】： 华南理工大学机械与汽车工程学院;
【分类号】：TG115

【参考文献】

相关期刊论文 前4条

1 马小明;黄志华;;聚丙烯挤出机螺杆轴断裂失效分析[J];机械工程材料;2014年10期

2 袁卫明;傅纪国;;注塑机螺杆强度的分析计算[J];轻工机械;2012年02期

3 刘阳春;铝型材挤压模的选材及其热处理[J];国外金属热处理;2001年05期

4 陈煜国,李相麟,扶名福;微孔洞型的分形断裂理论初探[J];应用力学学报;1998年04期

相关硕士学位论文 前2条

1 谢兆兴;高扭矩深槽啮合同向双螺杆设计及受力分析[D];北京化工大学;2011年

2 王申存;低碳低合金渗碳钢的组织、性能与晶体学特征的研究[D];中南大学;2010年

【共引文献】

相关期刊论文 前6条

1 马小明;周阳;;高速双螺杆挤出机螺杆轴断裂失效分析[J];机械工程材料;2017年03期

2 郭奕文;邓运来;王宇;刘胜胆;;2024铝合金航空座椅支承零件等温模锻成形研究[J];锻压技术;2016年08期

3 马小明;肖鹏;;38CrMoAlA挤出机螺杆轴断裂失效分析[J];热加工工艺;2016年10期

4 马小明;黄志华;;聚丙烯挤出机螺杆轴断裂失效分析[J];机械工程材料;2014年10期

5 王红斌;刘海燕;;分形理论在有机玻璃有效弹性模量及裂纹聚合路径研究中的应用[J];玻璃;2014年06期

6 郭隽,郭成璧;高温疲劳表面短裂纹的分形研究[J];固体力学学报;2002年02期

【二级参考文献】

相关期刊论文 前10条

1 杨s，

本文编号：1567838