磁场对硫酸盐还原菌生物膜在304不锈钢表面吸附性能的影响

发布时间：2018-03-19 01:00

  本文选题：静态磁场　切入点：硫酸盐还原菌　出处：《中国腐蚀与防护学报》2016年06期 　论文类型：期刊论文

【摘要】：采用表面分析和电化学手段研究了静态磁场对硫酸盐还原菌(SRB)在304不锈钢表面吸附性能的影响。结果表明:磁场强度为150 mT对浮游SRB的生长没有明显的影响,但是可以延迟固着SRB的形成;静态磁场可以抑制SRB生物膜在304不锈钢表面的形成和吸附,磁场强度为4 mT时比150 mT时的效果更好。使用X射线光电子能谱(XPS)对腐蚀产物进行分析表明,在静态磁场条件下腐蚀产物中有铁氧化物生成。
[Abstract]:The effect of static magnetic field on the adsorption properties of sulfate-reducing bacteria SRB on 304 stainless steel was studied by surface analysis and electrochemical methods. The results showed that the magnetic field intensity of 150mT had no obvious effect on the growth of SRB. The static magnetic field can inhibit the formation and adsorption of SRB biofilm on the surface of 304 stainless steel. When the magnetic field intensity is 4 Mt, the effect is better than that at 150 Mt. The analysis of corrosion products by X-ray photoelectron spectroscopy (XPS) shows that iron oxides are formed in the corrosion products under static magnetic field.
【作者单位】： 华中科技大学化学与化工学院材料服役与失效湖北省重点实验室;深圳华中科技大学研究院;海军工程大学理学院;
【基金】：国家自然科学基金项目(51171067) 深圳市基础研发基金项目(JC201005310696A) 华中科技大学创新基金项目(国合专项2015ZZGH010,前沿探索类2015TS150) 材料化学与服役失效湖北省重点实验室基金项目(201502)资助
【分类号】：TG142.71;TG174.4

【相似文献】

相关期刊论文 前10条

1 李林;;油田生产中硫酸盐还原菌的危害及其防治[J];化工时刊;2010年09期

2 N.N.Lyalikova;裘荣庆;;应用硫酸盐还原菌富集矿石[J];国外金属矿选矿;1979年07期

3 刘魁元;;硫酸盐还原菌抑制剂的研究与应用概况[J];工业水处理;1984年04期

4 李文融;硫酸盐还原菌[J];工业水处理;1986年01期

5 李凡修;;预防石油开采中硫酸盐还原菌生长的抑制剂[J];钻采工艺;1990年03期

6 师祥洪;;浅谈油田注水系统中硫酸盐还原菌的取样方法[J];油气田环境保护;1992年04期

7 刘宏芳,黄茁,许立铭,郑家q，

本文编号：1632089