60Si2CrVA弹簧钢断口及断裂原因分析

发布时间：2018-03-27 10:26

  本文选题：SiCrVA弹簧　切入点：断口　出处：《材料热处理学报》2016年04期

【摘要】：60Si2Cr VA弹簧在服役状况下,运行寿命不到设计寿命的1/3,发生了断裂。为了分析弹簧的断口和断裂原因,根据该弹簧钢的制造和服役状况,对断口宏观形貌、SEM照片进行了分析;并对弹簧钢的应力分布、化学成分、组织和硬度进行了分析。发现了弹簧断裂为疲劳断裂,其失效起源于表面缺陷和最大切应力的共同作用,且弹簧内部组织有石墨化现象,硬度高,韧性降低,导致了整个工件的断裂。提出了该弹簧在加工过程、检测过程及热处理过程中的一些改进的措施。
[Abstract]:Under the condition of service, the service life of the 60Si2Cr VA spring is less than 1 / 3 of the designed life. In order to analyze the fracture surface and the cause of the fracture, according to the manufacture and service condition of the spring steel, the macroscopic morphology of the fracture surface is analyzed. The stress distribution, chemical composition, microstructure and hardness of spring steel are analyzed. It is found that spring fracture is fatigue fracture, its failure originates from the joint action of surface defect and maximum shear stress, and the internal structure of spring is graphitized. High hardness and low toughness lead to the fracture of the whole workpiece. Some measures to improve the spring in the process of processing, testing and heat treatment are put forward.
【作者单位】： 北京科技大学新材料技术研究院;北京市腐蚀磨蚀与表面技术重点实验室;
【基金】：北京市腐蚀、磨蚀与表面技术重点实验室和北京市教委共建项目(SYS100080419)
【分类号】：TG142.15

【相似文献】

相关期刊论文 前9条

1 宛农,雷应华;60Si2CrVA弹簧钢回火特性的模拟和分析[J];机车车辆工艺;2004年04期

2 张炼,杨思齐,郦振声;高强度弹簧钢60Si2CrVA的性能[J];机械工程材料;1992年04期

3 张炼;杨思齐;郦振声;;60Si2CrVA弹簧钢循环细晶热处理[J];金属科学与工艺;1992年01期

4 周超;张永健;惠卫军;王磊;;氢对60Si2CrVA弹簧钢超高周疲劳性能的影响[J];钢铁研究学报;2013年09期

5 张占玲;赵飞;谭文龙;;热处理工艺对60Si2CrVA弹簧钢组织及性能的影响[J];金属热处理;2014年05期

6 赵海民;惠卫军;聂义宏;翁宇庆;董瀚;;60Si2CrVA高强度弹簧钢的超高周疲劳破坏行为[J];材料研究学报;2008年05期

7 余国松;毛文俊;李秦欢;余其中;;60Si2CrVA弹簧钢轧制过程脱碳的研究[J];浙江冶金;2013年02期

8 李国刚;温殿英;;弹簧钢60Si2CrVA缺陷及对失效的影响[J];天津理工大学学报;2008年01期

9 ;[J];;年期

相关会议论文 前2条

1 林宪;郭昭桥;林水石;余其中;;60Si2CrVA弹簧钢力学性能影响因素研究[A];2007中国钢铁年会论文集[C];2007年

2 郝立群;惠卫军;项金钟;李英;惠荣;翁宇庆;董瀚;;不同冶金工艺生产的60Si2CrVA弹簧钢的高周疲劳破坏行为研究[A];第十四届全国疲劳与断裂学术会议论文集[C];2008年

，

本文编号：1671122