复合热处理对ZG20CrSiMn耐磨铸钢组织和性能影响

发布时间：2018-03-27 19:05

  本文选题：低碳铸钢　切入点：亚温淬火　出处：《材料热处理学报》2017年03期

【摘要】：采用金属模具浇注新型ZG20CrSiMn槽帮低碳耐磨铸钢,研究了亚温淬火热处理(QLT)和深冷处理(DCT)复合热处理对其显微组织、力学性能和耐磨损性能的影响。结果表明,与常规调质(QT)、QT+DCT及QLT工艺相比,复合热处理(QLT+DCT)工艺可以显著提高ZG20CrSiMn钢的抗拉强度、韧性以及抗磨损性能。经QLT+DCT工艺处理后的ZG20CrSiMn钢,具有良好的抗拉强度及韧性,这与层片状的细小回火索氏体组织和一定比例的铁素体有关。与QT+DCT工艺处理样品对比,QLT+DCT工艺处理样品具有更好的耐磨损性能。
[Abstract]:A new type of low carbon wear-resistant cast steel with ZG20CrSiMn groove was cast by metal die. The effects of subtemperature quenching heat treatment (QT) and cryogenic treatment on microstructure, mechanical properties and wear resistance of the steel were studied. Compared with the conventional quenched and tempered QT / QT DCT and QLT processes, the composite heat treatment / QLTDCT process can significantly improve the tensile strength, toughness and wear resistance of the ZG20CrSiMn steel. The ZG20CrSiMn steel treated by the QLT DCT process has good tensile strength and toughness. These results are related to the microstructure of fine tempering solids and a certain proportion of ferrite. Compared with the samples treated by QT DCT process, the samples treated by QLT DCT process have better wear resistance.
【作者单位】： 山西工程技术学院;太原理工大学材料科学与工程学院;太原科技大学材料科学与工程学院;
【基金】：2014年度山西省煤基重点科技攻关项目(MC2014-02) 太原科技大学校博士科研启动项目(20152011)
【分类号】：TG142.1;TG161

【相似文献】

相关期刊论文 前10条

1 王云霖;闩体的复合热处理[J];兵器材料科学与工程;1985年04期

2 高彩桥,靳忠效;复合热处理[J];机械工程师;1986年01期

3 梁淑荣,李新生;精密冷挤零件的复合热处理工艺[J];金属热处理;2000年08期

4 李新生,梁淑荣;精密冷挤零件的复合热处理工艺[J];机械工艺师;2001年01期

5 蒋宁;;复合热处理工艺与节能环保良性互动[J];重庆三峡学院学报;2009年03期

6 高彩桥;复合热处理与复合化学热处理[J];固体润滑;1986年02期

7 鲋田清司;易泓可;;复合热处理动向[J];国外金属热处理;1986年01期

8 何则荣;蔡传荣;;40Cr钢复合热处理强韧化[J];金属科学与工艺;1987年03期

9 何则荣;钢复合热处理强韧化的研究[J];福州大学学报(自然科学版);1988年03期

10 林吉清;针板新工艺—多工序相变复合热处理[J];机械设计与研究;1991年03期

相关硕士学位论文 前1条

1 谢仔新;基于GM标准的高强度汽车紧固件复合热处理生产技术研究[D];浙江工业大学;2013年

，

本文编号：1672829