硫脲基松香咪唑啉季铵盐对A3碳钢的缓蚀性能

发布时间：2018-03-29 13:49

  本文选题：硫脲基松香咪唑啉季铵盐　切入点：缓蚀性能　出处：《精细化工》2017年03期

【摘要】：以松香、二乙烯三胺、3-氯-2-羟基丙烷磺酸钠和硫脲为原料,经酰胺化、季铵化和脱氨缩合3步反应合成了硫脲基松香咪唑啉季铵盐,并用红外和核磁对其结构进行了表征。采用失重法、动电位极化曲线、交流阻抗以及接触角测试分析了目标产物在质量分数为15%的盐酸溶液中对A3碳钢的缓蚀性能。采用AFM及XPS对产物的吸附膜进行了表征。结果表明:目标产物的缓蚀率随其质量分数的增加先增大后减小,当目标产物质量分数增至占盐酸质量的0.4%时,缓蚀率最高达到90.78%;该物质是一种阴极控制为主的混合型缓蚀剂;AFM及XPS结果证实,目标产物确实可以在碳钢表面形成缓蚀剂吸附膜。
[Abstract]:The thiourea-base rosin imidazoline quaternary ammonium salt was synthesized from rosin, diethyltriamine 3-chloro-2-hydroxypropane sulfonate and thiourea by amidation, quaternization and deamination. The structure was characterized by IR and NMR. The potentiodynamic polarization curve was determined by weightlessness method. The corrosion inhibition of A3 carbon steel in hydrochloric acid solution with 15% mass fraction was analyzed by AC impedance and contact angle measurement. The adsorption film of A3 steel was characterized by AFM and XPS. The results showed that the target product was retarded. The corrosion rate increases first and then decreases with the increase of mass fraction. When the mass fraction of the target product increased to 0.4% of the hydrochloric acid mass, the corrosion inhibition rate reached 90.78%, and the result of AFM and XPS showed that the target product could form corrosion inhibitor adsorption film on the surface of carbon steel.
【作者单位】： 陕西科技大学教育部轻化工助剂化学与技术重点实验室;
【基金】：陕西省科技统筹创新工程计划项目(2014KTCL01-11) 陕西省科学技术研究发展计划项目(2013K11-19)~~
【分类号】：TG174.42

【相似文献】

相关期刊论文 前10条

1 吕洪久;;日本将用新法制造咪唑啉酮[J];精细与专用化学品;1985年06期

2 徐长卿;用椰子油直接合成咪唑啉及其衍生物[J];日用化学工业;1985年02期

3 马慰霖;沈中原;庄义婷;;2-咪唑啉酮合成的新工艺[J];农药;1986年03期

4 任晋斌;咪唑啉型香波原料安全性试验[J];日用化学工业;1987年05期

5 储宁启,张晓生,李湘林;咪唑啉环化釜改造[J];日用化学工业;1990年05期

6 丁渝;沈苗;周宁;;1-苄基-5-乙氧基-2,4-咪唑啉二酮的合成[J];化学试剂;1993年01期

7 赵炳筠,郭艳玲,王进东,夏炽中;1,2,3—三取代咪唑啉盐的质谱研究[J];山西大学学报(自然科学版);1997年03期

8 谢晖,何文深,周永红;松香基咪唑啉的合成及应用[J];南京工业大学学报(自然科学版);2004年06期

9 焦其正;付朝阳;王丽荣;郑家q，

本文编号：1681397