邹莹,董选普,张洁,樊自田,王爱华,气流搅拌镁合金半固态铸造新技术

  本文关键词：气流搅拌镁合金半固态铸造新技术，，由笔耕文化传播整理发布。

首页 > 专家 > 内容

文献名称：气流搅拌镁合金半固态铸造新技术

    前言：提出了吹气鼓泡方式下产生的强对流、弱搅拌而获得AZ91D镁合金半固态组织的新工艺。研究了在不用搅拌温度和冷却介质下吹气鼓泡方式对半固态组织的影响。结果表明,吹气搅拌温度在600℃～610℃时,能够获得不同程度的半固态组织。对吹气鼓泡方式下获得镁合金组织的机理作了初步分析,为进一步扩充研究该方法提供基础。
    The new technique for agitating semi-solid magnesium alloy AZ91D slurry by gas blowing which create strong convection and weak agitation during solidification was put forward in this article.The effects of different agitating temperatures and molten Mg alloy cooling media on semi-solid microstructure were discussed.The results showed that AZ91D semi-solid microstructure by introducing Ar gas bubbles could be obtained at an agitating temperature between 600 ℃~610 ℃,and the mechanism of obtaining semi-solid M...

文献名称 气流搅拌镁合金半固态铸造新技术

Article Name
英文(英语)翻译 A New Casting Technique of Agitating Semi-Solid Magnesium Alloy Using a Gas Blowing Method;

作者 邹莹; 董选普; 张洁; 樊自田; 王爱华;

Author ZOU Ying;DONG Xuan-pu;ZHANG Jie;FAN Zi-tian;WANG Ai-hua（State Key Laboratory of Material Processing and Die & Mould Technology;Huazhong University of Science and Technology;Wuhan 430074;Hubei;China）;

作者单位
Author Agencies 华中科技大学材料成型及模具技术国家重点实验室; 华中科技大学材料成型及模具技术国家重点实验室 湖北武汉; 湖北武汉;

文献出处
Article From 中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度

关键词 AZ91D镁合金; 半固态; 气流搅拌法; 微观组织;

Keywords AZ91D magnesium alloy;semi-solid;gas bubble method;microstructure;

AZ91D镁合金表面机械研磨处理后显微结构研究
AZ91D镁合金直接化学镀镍工艺研究
AZ91D镁合金表面化学转化处理及镀镍
激光熔覆AZ91D镁合金的界面特征和耐磨性研究
AZ91D镁合金表面磷化膜组织结构与性能的研究
Al-8Ti-2C中间合金对AZ91D镁合金的组织和性能的影响
以锡酸钠为主盐的AZ91D镁合金化学转化处理工艺
等温热处理对消失模铸造AZ91D镁合金组织与性能的影响
AZ91D镁合金触变铸造件热处理前后的组织与性能
触变成形AZ91D镁合金的组织与二次凝固行为

  本文关键词：气流搅拌镁合金半固态铸造新技术，由笔耕文化传播整理发布。