Hi-B钢动态再结晶的研究及动态回复模型的建立

发布时间：2018-03-31 22:10

  本文选题：Hi-B钢　切入点：动态回复　出处：《上海金属》2016年05期

【摘要】：采用单道次热压缩实验在Gleeble-1500热力模拟机上研究了不同变形速率和变形温度下Hi-B钢的软化行为。结果表明,试验钢在较低应变速率下,主要以动态回复作为软化机制,在较高应变速率下,主要以动态再结晶作为软化机制。采用回归法计算出动态回复的变形激活能和应变指数分别为287.12 k J/mol和4.88,由此建立了试验钢在低应变速率下的动态回复模型。
[Abstract]:The softening behavior of Hi-B steel at different deformation rates and deformation temperatures was studied by single pass thermal compression experiment on a Gleeble-1500 thermal simulator. The results show that dynamic recovery is the main softening mechanism of the tested steel at low strain rate. At higher strain rates, Using dynamic recrystallization as softening mechanism, the deformation activation energy and strain exponent of dynamic recovery were calculated to be 287.12 k J/mol and 4.88 k respectively by regression method. The dynamic recovery model of test steel at low strain rate was established.
【作者单位】： 武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室;
【基金】：国家自然科学基金资助项目(No.51274155)
【分类号】：TG142.1

【相似文献】

相关期刊论文 前10条

1 刘效东,方鸿生,陈南平;低碳锰硼钢中温奥氏体区的动态回复行为[J];材料科学进展;1990年04期

2 刘文昌;郑炀曾;;45V钢热变形条件下的动态回复行为[J];金属热处理学报;1993年03期

3 汪日志,雷廷权;金相及电镜法研究低碳钢铁素体的动态回复过程[J];理化检验(物理分册);1994年04期

4 田永君;袁秀信;高慧菊;吴浩泉;;热变形中的动态回复过程[J];金属科学与工艺;1987年02期

5 彭一波;王罡;潘尚峰;融亦鸣;;考虑动态回复过程的6005A铝合金动态力学模型[J];机械工程学报;2014年10期

6 孙东升,李木森,邹勇,杨锐,李凤照;bcc结构的动态回复模型[J];科学通报;1997年14期

7 韩明臣;;钛合金热变形时的动态回复和再结晶[J];稀有金属快报;2007年12期

8 万伦;徐光;陈振业;刘莉;吴开兵;;CSP微合金钢变形抗力动态回复模型[J];特殊钢;2009年01期

9 沈健，张新明，章四琪，，尹志民，卢斌，宋恒早，舒先进;工业纯Al高温扭转时的动态回复和动态再结晶[J];金属学报;1995年09期

10 金朝阳;崔振山;;低碳钢热塑性成形过程本构模型[J];上海交通大学学报;2010年04期

相关硕士学位论文 前1条

1 陈庆勇;冷轧态TWIP钢回复再结晶行为研究[D];西南石油大学;2012年

本文编号：1692674