焊料对锰铝青铜补焊件显微组织和力学性能的影响（英文）

发布时间：2018-04-04 03:18

  本文选题：锰铝青铜　切入点：焊接　出处：《Transactions of Nonferrous Metals Society of China》2017年03期

【摘要】：使用不同金属焊料对UNS C95700锰铝青铜板进行补焊,研究焊件的显微组织和力学性能。结果表明,焊件主要显微组织为具有不同形貌的α,β和κ相。锰的加入使焊件显微组织中α相的含量由80%(无Mn焊件)降低到57%(12.5%Mn焊件)。在高镍焊件中κ相的形貌为层状,而在高锰焊件中κ相形貌变为球状。相对于使用高镍焊料获得的焊件,采用高锰焊料获得的焊件具有较高的抗拉强度和弯曲强度。当以非合金焊料ERCuAl-A2为衬底、高锰焊料(ERCuMnNiAl)为填充焊道进行补焊时,焊件的力学性能最佳。此焊件的抗拉强度比基体金属的抗拉强度提高了39%,且弯曲试验后仍未发生开裂现象。
[Abstract]:The microstructure and mechanical properties of UNS C95700 manganese aluminum bronze plate were studied by using different metal solders.The results show that the main microstructure of the welded part is 伪, 尾 and 魏 phase with different morphologies.The addition of manganese reduced the content of 伪 phase in the microstructure from 80% (without mn) to 57%(12.5%Mn welding piece.The morphology of 魏 phase is layered in high nickel welds and globular in high manganese welds.Compared with that obtained with high nickel solder, the high manganese solder has higher tensile strength and bending strength.When the non-alloy solder ERCuAl-A2 is used as the substrate, and the high manganese solder ERCuMnNiAl is used as the filler, the mechanical properties of the welding piece are the best.The tensile strength of the welded part is 39% higher than that of the base metal, and no cracking has occurred after bending test.
【作者单位】： Materials
【分类号】：TG455

【相似文献】

相关期刊论文 前10条

1 ;力学性能二级人员取证复习参考题(之一)解答[J];理化检验(物理分册);1997年12期

2 ;力学性能二级人员取证复习参考题(之三)解答[J];理化检验(物理分册);1998年04期

3 陈金宝;高温力学性能二级人员取证复习参考题(持久部分之五)解答[J];理化检验(物理分册);2000年02期

4 潘叶金;电弧熔铸的Nb-18Si-5Mo-5Hf-2C复合材料的力学性能[J];中国钼业;2003年03期

5 张美忠,李贺军,李克智;三维编织复合材料的力学性能研究现状[J];材料工程;2004年02期

6 游宇,周新贵;三维编织复合材料的力学性能[J];纤维复合材料;2004年04期

7 罗文波;唐欣;谭江华;赵荣国;;流变材料长期力学性能加速表征的若干进展[J];材料导报;2007年07期

8 严振宇;徐强;朱时珍;刘颖;;Sm_2Zr_2O_7-ZrB_2/SiC复合材料的制备及力学性能研究[J];稀有金属材料与工程;2011年S1期

9 瞿欣;孙汝n，

本文编号：1708132