预应力加载条件下零件干磨削表面强化层特征

发布时间：2018-04-08 19:11

  本文选题：预应力淬硬磨削　切入点：位错　出处：《东北大学学报(自然科学版)》2017年01期

【摘要】：采用预应力复合干磨削加工技术,对未调质45#钢试件在不同预应力加载条件下实施表面磨削淬硬,观测不同磨削深度和进给速度条件下的试件表层金相组织,测量并分析试件在不同预应力条件下磨削淬硬层厚度、金相组织的变化状况,并通过试件截面不同位置硬度测定显示淬硬层厚度及金相成分的变化,得到试件施加预应力对淬硬强化层厚度的影响规律.研究表明,预应力淬硬磨削能使工件表面产生强化层,且大的磨削深度和小的进给速度有利于试件表面发生相变强化以及表层塑性变形的增大.
[Abstract]:In this paper, the surface grinding and hardening of untempered 4 steel specimens under different prestressing loading conditions are carried out by using the prestressing composite dry grinding technology. The microstructure of the surface surface of the specimens under different grinding depth and feed rate is observed.The change of hardened layer thickness and metallographic structure under different prestressing conditions were measured and analyzed, and the changes of hardened layer thickness and metallographic composition were shown by hardness measurement at different positions of the specimen section.The effect of prestress on the thickness of hardened layer is obtained.
【作者单位】： 东北大学机械工程与自动化学院;辽宁科技学院机械工程学院;新疆工程学院机械工程系;
【基金】：国家自然科学基金资助项目(51375083) 辽宁省教育厅科学研究一般项目(L2015274)
【分类号】：TG580.6

【相似文献】

相关期刊论文 前9条

1 时海芳;刘波;李海玉;孙上茹;;磨削深度对42CrMo钢磨削强化层的影响[J];金属热处理;2012年01期

2 李良福;;磨具临界磨削深度的计算[J];精密制造与自动化;2006年04期

3 杨刚;韩正铜;杜长龙;;进给速度与磨削深度对40Cr钢磨削强化效果的影响[J];煤矿机械;2008年03期

4 刘菊东,王贵成,陈康敏;磨削深度对65Mn钢磨削硬化层的影响[J];农业机械学报;2005年08期

5 刘菊东,王贵成,陈康敏,贾志宏;45钢磨削硬化的试验研究[J];材料科学与工艺;2005年03期

6 刘克铭;马壮;张连勇;刘波;;磨削深度及原始组织对42CrMo磨削淬硬层的影响[J];热加工工艺;2012年10期

7 吴玉厚;吕艳;;HIP-SN陶瓷轴承套圈磨削特性的实验[J];沈阳建筑大学学报(自然科学版);2007年01期

8 高国富,赵波,刘传绍,焦锋;细磨粒超声珩磨ZrO_2表面特征研究[J];金刚石与磨料磨具工程;2003年03期

9 ;[J];;年期

相关会议论文 前1条

1 刘菊东;侯达盘;;磨削深度和原始组织对60钢磨削淬硬层的影响[A];2008年中国机械工程学会年会暨甘肃省学术年会文集[C];2008年

相关博士学位论文 前1条

1 刘克铭;42CrMo钢磨削淬火及仿真研究[D];辽宁工程技术大学;2014年

相关硕士学位论文 前2条

1 张海南;超硬微结构光学功能表面的ELID磨削加工技术研究[D];哈尔滨工业大学;2013年

2 刘波;42CrMo钢磨削淬火及数值模拟[D];辽宁工程技术大学;2012年

，

本文编号：1722969