一种新型冷作模具钢DC53钢试验研究

发布时间：2018-04-11 03:13

本文选题：冲压模具 + 模具材料　；参考：《锻压装备与制造技术》2016年05期

【摘要】：本文介绍了一种新型冷作模具钢DC53钢的物理性能和热处理工艺,探索了DC53钢作为模具镶块材料的使用寿命。与冷作模具钢7Cr Si Mn Mo V进行了性能比较试验,结果表明,相同工况下,DC53钢寿命是7Cr Si Mn Mo V钢的5~6倍,使用DC53钢代替7Cr Si Mn Mo V钢在铁路货车用冷冲压模具中是可行的。
[Abstract]:The physical properties and heat treatment process of a new cold working die steel DC53 steel are introduced in this paper. The service life of DC53 steel as die insert material is explored.The performance comparison test with cold working die steel 7Cr Si mn Mo V shows that the life of 7Cr Si mn Mo V steel is 5 ~ 6 times longer than that of 7Cr Si mn Mo V steel under the same working condition. It is feasible to use DC53 steel instead of 7Cr Si mn Mo V steel in cold stamping die for railway freight car.