分区扫描路径规划及其对SLM成型件残余应力分布的影响

发布时间：2018-04-12 17:35

  本文选题：激光技术 + 分区扫描　； 参考：《中国激光》2016年12期

【摘要】：为了解决激光选区熔化成型零件时扫描线过长导致的层内累积残余应力过大、易发生翘曲变形和裂纹等问题,提出了一种分区扫描策略。采用S形正交扫描策略和分区扫描策略分别规划了零件扫描路径,实验验证了分区扫描策略的有效性。实验结果表明,采用分区扫描策略能有效降低边界拉应力,减小平面残余应力波动,提高成型件的力学性能。
[Abstract]:In order to solve the problem that the accumulated residual stress in the layer is too large and the warping deformation and crack are easy to occur due to the excessive scanning line during the laser selective melting molding, a zonal scanning strategy is proposed.The S-shape orthogonal scanning strategy and the partitioned scanning strategy are used to plan the scanning path of the parts, and the effectiveness of the partitioned scanning strategy is verified by experiments.The experimental results show that the zonal scanning strategy can effectively reduce the boundary tensile stress, reduce the fluctuation of plane residual stress, and improve the mechanical properties of the molded parts.
【作者单位】： 华南理工大学机械与汽车工程学院;
【分类号】：TH164;;TN249

【相似文献】

相关会议论文 前1条

1 丁锦红;;视觉扫描路径重复效应研究[A];第十二届全国心理学学术大会论文摘要集[C];2009年

相关硕士学位论文 前5条

1 侯章浩;熔融沉积成型的路径规划研究[D];新疆大学;2015年

2 李雨澄;飞秒激光双光子聚合加工扫描路径的规划[D];长春工业大学;2016年

3 张曼;RP中扫描路径的生成与优化研究[D];西安科技大学;2006年

4 李阳;基于几何图形相似性的扫描路径选择与检索的研究[D];西安理工大学;2009年

5 张连重;基于机器人堆焊的快速再制造成形分层路径规划研究[D];新疆大学;2013年

，

本文编号：1740739