焊后热处理温度对SWRH82B盘条电阻对焊接头组织与力学性能的影响

发布时间：2018-04-14 16:37

  本文选题：SWRHB盘条 + 电阻对焊　； 参考：《热加工工艺》2017年21期

【摘要】：为了提高SWRH82B盘条电阻对焊接头的性能,对SWRH82B盘条进行了电阻对焊和焊后热处理,分析了不同焊后热处理温度下的焊接接头组织、拉伸断口形貌和力学性能。结果显示,焊后热处理温度对焊接接头组织的粗大程度、铁素体和二次渗碳体的析出程度具有较大的影响。在合适的热处理温度下其焊接接头组织较细小均匀,铁素体和二次渗碳体的析出量小,塑性好。
[Abstract]:In order to improve the performance of SWRH82B wire rod resistance butt welding joint, the resistance butt welding and post welding heat treatment of SWRH82B wire rod were carried out. The microstructure, tensile fracture morphology and mechanical properties of the welded joint at different post-weld heat treatment temperature were analyzed.The results show that the temperature of post-weld heat treatment has a great influence on the coarse degree of microstructure and the precipitation degree of ferrite and secondary cementite.At the appropriate heat treatment temperature, the microstructure of the welded joint is fine and uniform, the amount of precipitation of ferrite and secondary cementite is small, and the plasticity is good.
【作者单位】： 九江学院;
【基金】：九江学院校级科研项目(2013ZD07,2014KJYB018) 江西省教育厅科技落地计划项目(KJLD14091) 江西省科技计划项目(20133BBE50031) 江西省“卓越工程师教育培养计划”实施成果(赣财教2011[244]号)
【分类号】：TG407

【相似文献】

相关期刊论文 前10条

1 袁庆扬;;高碳钢丝的电阻对焊研究[J];金属制品;1985年01期

2 唐利;;70钢钢丝电阻对焊裂纹产生原因分析及处理[J];焊接技术;2010年08期

3 唐利;;汽车环形钢丝零件电阻对焊后裂纹产生原因分析及改进措施[J];理化检验(物理分册);2010年11期

4 杨辉;;高碳钢盘条电阻对焊质量的影响因素分析[J];热加工工艺;2012年17期

5 李，

本文编号：1750185