文献名称：铁型覆砂铸造磨球工艺的试验研究

    前言：应用铁型覆砂铸造技术和计算机磨球工艺装备和试验装置,进行了现场工艺试验,获得了关键工艺参数数据。试验结果表明,新工艺生产的磨球尺寸精度可以达到CT6级,表面粗糙度达到Ra12.5,球铁材质铸态硬度(HRC)平均值为32～34,直径60mm磨球的工艺出品率达到70%,生产工序少、周期短,适合机械化生产线方式进行大规模生产。
    Using the casting technology of sand-coated iron-mold and the computer simulation technology, studied the casting technology of iron mould coated sand to rub the ball craft the principle, developed the iron mould coated sand casting bainite nodular cast iron according to the production line standard to rub the ball craft equipment and the test equipment, it has carried on the scene engineer testing and has obtained the essential craft parameter data. The test result indicated that the new craft production r...

文献名称 铁型覆砂铸造磨球工艺的试验研究

Article Name
英文(英语)翻译 Experimental Study on Casting Grinding Balls Craft with Iron Mould Coated Sand;

作者 林方夫; 胡建新; 马益诚; 高强; 潘东杰; 黄列群;

Author LIN Fang-fu1;HU Jian-xin2;MA Yi-cheng1;GAO Qia1;PAN Dong-jie1;HUANG Lie-qun1 （1. Zhejiang Institute of Mechanical & Electrical Engineering Co.;Ltd.;Hangzhou 310009;Zhejiang;China;2. Equipment Research Institute;Jinchuan Group Ltd.;Jinchang 737103;Gansu;China）;

作者单位
Author Agencies 浙江省机电设计研究院有限公司; 金川集团有限公司设备研究所; 浙江省机电设计研究院有限公司 浙江杭州; 甘肃金昌; 浙江杭州;

文献出处
Article From 中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度

关键词 铸造磨球; 铁型覆砂; 工艺试验;

Keywords casting grinding balls;iron mould coated sand;experimental study;

消失模铸造磨球
提高消失模铸造磨球质量的工艺研究
消失模铸造磨球的生产实践
立式离心铸造磨球充型过程的影响因素研究
立式离心金属型铸造磨球生产线的设计
钨渣低铬铸造磨球材质的研究
离心铸造磨球充型规律的研究
纳米氧化物改性水玻璃的作用机理研究
关于高质量汽缸体铸造工艺问题的探讨
提高电弧炉炉衬寿命的措施

  本文关键词：铁型覆砂铸造磨球工艺的试验研究，由笔耕文化传播整理发布。