电接触强化对Ni-P镀层组织与性能的影响

发布时间：2018-04-14 17:38

  本文选题：Ni-P电刷镀层 + 电接触强化　； 参考：《热加工工艺》2017年22期

【摘要】：在40Cr表面通过电刷镀技术制备Ni-P镀层,利用电接触技术对该镀层进行强化。进一步通过光学显微镜、扫描电镜、能谱仪、X射线衍射分析和显微硬度测试仪研究了镀层强化前后的组织与性能。结果表明:通过电接触强化技术制备了一种高性能冶金镀层,镀层缺陷较少,硬度达780.79 HV0.1。镀层与基体的结合方式从机械结合变成冶金结合,镀层中产生了新相Ni_3P。
[Abstract]:The Ni-P coating was prepared on the surface of 40Cr by brush plating, and the coating was strengthened by electric contact technique.The microstructure and properties of the coating before and after strengthening were studied by means of optical microscope, scanning electron microscope, X-ray diffraction analysis and microhardness tester.The results showed that a kind of high performance metallurgical coating was prepared by means of electrical contact strengthening technology. The defects of the coating were less and the hardness was up to 780.79 HV0.1.The bonding mode between coating and substrate changed from mechanical bonding to metallurgical bonding, and a new phase Ni3Pin was produced in the coating.
【作者单位】： 东华大学机械工程学院;
【基金】：上海市重点学科建设资助项目(B602)
【分类号】：TG174.44

【相似文献】

相关期刊论文 前10条

1 向文才;;对电接触炉有关公式的认识[J];金属制品;1989年03期

2 楚振斌;电接触磨削实验报告[J];机床与工具;1957年12期

3 赵志明;电接触炉电压公式的探讨及对传统公式的质疑[J];金属制品;1988年02期

4 赵志明;电接触炉电压公式中有关钢丝预热温度的探讨及计算[J];金属制品;1990年01期

5 钟玉川;;电接触切割设备[J];机械设计与制造;1988年01期

6 朱振荣;新型电接触薄膜保护剂的发展[J];宇航材料工艺;1987年05期

7 胡冀远;蔡建国;;利用电接触炉生产正火钢丝[J];金属制品;1991年05期

8 陈定一;居德明;;电接触电阻加热挤(滚)压高铬铸铁的实验研究[J];安徽工学院学报;1989年01期

9 钟灿贤;弹簧钢件在水介质中电接触处理法[J];国外金属热处理;1997年01期

10 陈定一;电接触电阻加热挤压镍、铬金合铸铁[J];机床;1987年02期

相关会议论文 前1条

1 于军琪;孙龙杰;席爱民;;钢丝电接触运动加热温度的模糊神经网络控制[A];全国冶金企业计控网络化研讨会论文集[C];2003年

相关硕士学位论文 前3条

1 朱浩;42CrMo钢表面涂层制备工艺的研究[D];东华大学;2017年

2 郝晓磊;电接触强化预涂层的制备[D];东华大学;2017年

3 罗湘;高性能镍基厚涂层的制备工艺及强化[D];东华大学;2017年

，

本文编号：1750385