火电厂汽轮机组叶片断裂分析与研究
发布时间:2018-04-16 12:04
本文选题:断裂叶片 + 断口 ; 参考:《热加工工艺》2017年20期
【摘要】:某火电厂汽轮机组在运行过程中,叶片发生断裂。为了分析叶片断裂原因,对断裂叶片进行宏观检查与分析、化学成分分析、硬度测试试验和金相显微组织观察与分析。结果表明:由于叶根内弧面存在表面损伤,加剧叶片振动,且叶根凹形槽下台阶是应力集中区,疲劳裂纹源在该处产生并逐渐扩展,导致叶片疲劳断裂;断口疲劳源区和疲劳裂纹扩展区所占面积大约为整个断口面积的三分之二,表明叶片断裂属于高周疲劳断裂。
[Abstract]:The blade of a steam turbine unit in a thermal power plant breaks during operation.In order to analyze the cause of blade fracture, macroscopical inspection and analysis, chemical composition analysis, hardness test and metallographic microstructure observation and analysis were carried out.The results show that the blade vibration is aggravated by the existence of surface damage on the inner arc of the blade root and the stress concentration zone is located at the bottom step of the concave groove of the blade root, where the fatigue crack source is produced and gradually expanded, which leads to the fatigue fracture of the blade.The fatigue source area and fatigue crack growth area of the fracture surface are about 2/3 of the total fracture area, indicating that the blade fracture belongs to the high cycle fatigue fracture.
【作者单位】: 龙岩学院机电工程学院;
【分类号】:TG115;TM621.3
【相似文献】
相关期刊论文 前6条
1 王红庆;;火电厂汽轮机末级静叶片(2Cr13)的修补焊接工艺[J];中国石油和化工标准与质量;2012年04期
2 刘显惠;;汽轮机反向叶片断裂分析[J];机械;1985年06期
3 刘晓睿;王勤;梁鹏飞;王琛;陈蔚;乔宝虹;;核电厂汽轮机的无损检测[J];科技信息;2014年02期
4 吴培远;WJ5A-1型850086号发动机空中故障原因分析[J];材料工程;1992年04期
5 杜晓明 ,董秀琦 ,朱丽娟 ,施庭芳 ,董红潮;气轮机隔板埋铸叶片断裂分析[J];特种铸造及有色合金;2002年04期
6 张卫方,陶春虎,习年生,高威,刘高远;断口反推疲劳应力及其在叶片断裂分析中的应用[J];材料工程;2003年01期
,本文编号:1758801
本文链接:https://www.wllwen.com/kejilunwen/jiagonggongyi/1758801.html