强酸性氯离子环境下低合金钢的点蚀行为

发布时间：2018-04-17 02:17

  本文选题：强酸性 + 氯离子　； 参考：《钢铁》2017年06期

【摘要】：参照国际海事组织(IMO)发布的《油轮货油舱耐蚀钢性能标准》中所规定的模拟内底板试验方法,对比研究了在强酸性高氯离子浓度的环境下,传统低合金钢和耐蚀低合金钢的腐蚀速率及点蚀行为随温度变化的规律。试验结果表明,添加铜、镍元素的耐蚀低合金钢腐蚀速率较传统低合金钢最高降低了90%以上,并且具有优于传统低合金钢的抑制点蚀增殖、扩展的性能。耐蚀低合金钢表面及点蚀坑内部分布有白色颗粒,为铜元素的再沉积所致。该纯铜颗粒分布于试验钢表面可以有效提高钢的腐蚀电位,在点蚀坑内部的富集可以有效抑制点蚀坑在深度方向上的扩展。
[Abstract]:With reference to the simulated inner floor test method stipulated in the performance Standard for corrosion resistant Steel for tanker cargo tanks issued by the International Maritime Organization (IMO), a comparative study was made under the environment of strong acid and high chloride ion concentration.The corrosion rate and pitting behavior of traditional low alloy steel and corrosion resistant low alloy steel vary with temperature.The results show that the corrosion rate of corrosion resistant low alloy steel with the addition of copper and nickel is more than 90% lower than that of the traditional low alloy steel, and the corrosion rate is superior to that of the traditional low alloy steel.White particles are distributed on the surface and pitting pit of low alloy steel, which is caused by copper redeposition.The distribution of the pure copper particles on the surface of the test steel can effectively increase the corrosion potential of the steel, and the enrichment in the pitting pit can effectively inhibit the expansion of the pitting pit in the depth direction.
【作者单位】： 钢铁研究总院工程用钢研究所;
【基金】：工信部“基于IMO标准的船用耐蚀钢应用技术研究”资助项目(工信部装[2014]162号)
【分类号】：TE988;TG142.33

【相似文献】

相关期刊论文 前5条

1 雷冰;马元泰;李瑛;王福会;常泽亮;谢俊峰;宋文文;周理志;;模拟高温高压气井环境中HP2-13Cr的点蚀行为研究[J];腐蚀科学与防护技术;2013年02期

2 王献f ;含铬油套管钢的CO_2腐蚀点蚀特征研究[J];全面腐蚀控制;2002年06期

3 孙冬柏,李静,俞宏英,路民旭,严密林,赵国仙;Ca~(2+)和Mg~(2+)对CO_2环境中点蚀形貌的影响[J];钢铁研究学报;2001年03期

4 张国超;林冠发;张涓涛;;超级13Cr油套管钢的点蚀行为研究[J];焊管;2013年07期

5 ;[J];;年期

相关硕士学位论文 前2条

1 王军;原油储罐底板内腐蚀环境中的点蚀行为研究[D];中国石油大学(华东);2014年

2 曹治栓;油罐底板点蚀深度的数值模拟预测研究[D];中国石油大学（华东）;2013年

，

本文编号：1761625