发布时间：2018-04-22 21:16

  本文选题：高强耐候钢 + 钒氮微合金化　； 参考：《钢铁》2017年05期

【摘要】：钒氮微合金化是高强耐候钢YQ450NQR1强化屈服强度的重要途径。钒氮微合金化对高强耐候钢YQ450NQR1性能的影响主要由钒和氮两部分构成,其中钒产生晶粒细化、析出强化的主要作用,氮强化钒的作用。通过高强耐候钢YQ450NQR1的钒氮积w(V)·w(N)研究,发现钒和氮质量分数的增加均可提高钢的屈服强度,同时钒和氮也呈乘积的方式对屈服强度产生影响。为保证高强耐候钢YQ450NQR1的屈服强度达到465 MPa,要求钒氮积w(V)·w(N)达到0.001 44以上。为提高连铸坯的高温塑性,降低铸坯裂纹发生的敏感性,氮质量分数需控制为0.012%~0.014%。
[Abstract]:Vanadium-nitrogen microalloying is an important way to strengthen yield strength of high strength weathering steel YQ450NQR1. The effect of vanadium and nitrogen microalloying on the YQ450NQR1 properties of high strength weathering steels is mainly composed of two parts: vanadium and nitrogen, in which vanadium produces grain refinement, precipitation strengthening and nitrogen strengthening. The vanadium and nitrogen yield strength of high strength weathering steel YQ450NQR1 was studied. It was found that the yield strength of steel could be increased by increasing the mass fraction of vanadium and nitrogen, and the yield strength was affected by the way of product of vanadium and nitrogen. In order to ensure that the yield strength of high strength weathering steel YQ450NQR1 reaches 465MPa, the vanadium nitrogen accumulation (WV) WN) is required to be more than 0.001 44. In order to improve the high temperature plasticity of continuous casting billet and reduce the sensitivity of crack occurrence, the mass fraction of nitrogen should be controlled to 0.012% and 0.014%.
【作者单位】： 清华大学材料学院;攀钢集团研究院有限公司重轨及铁路用钢研究所;
【基金】：国家自然科学基金 宝钢联合基金资助项目(50174031)
【分类号】：TG142.7

【相似文献】

中国期刊全文数据库 前10条

1 ;攀钢研制新一代高强耐候钢[J];特钢技术;2003年03期

2 陈勇;;耐候钢的发展及开发中的关键技术浅析[J];新疆钢铁;2006年04期

3 陈吉清,陈邦文,胡敏,宋育来;武钢铁路车辆用耐候钢的开发[J];钢铁研究;2003年05期

4 陆匠心,李爱柏,李自刚,温东辉;宝钢耐候钢产品开发的现状及展望[J];中国冶金;2004年12期

5 于千;;耐候钢发展现状及展望[J];钢铁研究学报;2007年11期

6 刘志勇;陈邦文;陈吉清;胡敏;宋育来;;武钢铁路车辆及集装箱用耐候钢的现状及发展[J];钢铁研究;2009年06期

7 张国臣;;热轧耐候钢薄规格轧制稳定性探讨[J];科技与企业;2013年20期

8 吴志友;;车用耐候钢的研制[J];江苏冶金;1987年01期

9 渡边常安;增田一^，

本文编号：1788975