海洋浪溅区Zn涂层加速腐蚀实验模拟研究

发布时间：2018-04-30 15:45

  本文选题：电弧喷涂 + Zn涂层　； 参考：《材料导报》2017年10期

【摘要】：采用RM-1型海洋加速腐蚀实验和连续中性盐雾实验模拟海洋飞溅区的腐蚀环境对电弧喷涂Zn涂层的加速腐蚀。同时采用灰色关联分析法和加速转换因子分析法对两种海洋加速腐蚀实验的模拟性和加速性进行了分析。结果发现:两种实验方法均能模拟海洋飞溅区的腐蚀环境,但RM-1型海洋加速腐蚀实验能较好地模拟浪花飞溅区的腐蚀情况,而连续中性盐雾实验对Zn涂层造成的腐蚀较为严重,其具有优良的腐蚀加速性。
[Abstract]:The accelerated corrosion of arc sprayed Zn coating was simulated by RM-1 model ocean accelerated corrosion test and continuous neutral salt spray test. At the same time, the simulation and acceleration of the two kinds of ocean accelerated corrosion experiments were analyzed by grey correlation analysis and accelerated conversion factor analysis. The results show that both of the two methods can simulate the corrosion environment in the sea splash zone, but the RM-1 accelerated corrosion test can well simulate the corrosion situation in the spray splash zone, and the corrosion of Zn coating caused by continuous neutral salt spray test is more serious. It has excellent corrosion acceleration.
【作者单位】： 装甲兵工程学院装备再制造技术国防科技重点实验室;重庆大学材料科学与工程学院;
【基金】：国家自然科学基金优秀青年基金项目(51222510) 中国工程院咨询研究项目(2015-09-XY-003;2015-06-ZD-01)
【分类号】：TG174.4

【相似文献】

相关期刊论文 前7条

1 骆鸿;李晓刚;董超芳;肖葵;;304不锈钢在热带海洋大气下暴露实验和加速腐蚀实验研究[J];中国腐蚀与防护学报;2013年03期

2 郭军科;于金山;彭翔;尹力;曹顺安;;加速腐蚀实验研究碳钢的大气腐蚀行为[J];表面技术;2014年04期

3 谢春生;朱才进;洪昌;马恒毅;朱林放;;22MnCrNiMo系泊链钢的盐雾加速腐蚀实验研究[J];江苏科技大学学报(自然科学版);2011年03期

4 张全成,吴建生,杨晓芳,陈家光,李爱柏,王建军,郑文龙,魏云;耐大气腐蚀用钢实验室加速腐蚀的研究[J];材料保护;2002年03期

5 张东曙,蔡兰坤,祝鸿范,周浩;银表面防变色膜PMM性能研究[J];中国腐蚀与防护学报;2002年05期

6 李松梅;辛长胜;刘建华;于美;文陈;;不同阴离子对40CrNi2Si2MoVA钢腐蚀行为的影响[J];材料热处理学报;2013年10期

7 ;[J];;年期

，

本文编号：1825156