17CrNiMo6齿轮轴断裂原因分析及改进

发布时间：2018-05-01 12:15

  本文选题：CrNiMo + 断裂　； 参考：《包装工程》2017年07期

【摘要】：目的研究常用的减速机高速工作中,材料为17CrNiMo6齿轮轴断齿现象的原因以及改进措施。方法通过化学成分分析、硬度检测、显微组织分析等方法,研究分析17CrNiMo6齿轮轴断齿现象的原因,并根据产生断齿的原因提出改进措施。结果 17CrNiMo6齿轮轴断裂为疲劳断裂,断齿的主要因素为调制热处理工艺不当、非金属杂物超标产生应力集中现象等。结论通过改进热处理工艺、优化结构设计、提高加工精度等措施可改善17CrNiMo6齿轮轴的断齿现象。
[Abstract]:Objective to study the causes and improvement measures of 17CrNiMo6 gear shaft breaking teeth in high speed reducer. Methods by means of chemical composition analysis, hardness detection and microstructure analysis, the causes of tooth breakage in 17CrNiMo6 gear shaft were studied, and the improvement measures were put forward according to the causes of tooth breakage. Results the fracture of 17CrNiMo6 gear shaft was fatigue fracture. The main factors of breaking teeth were improper modulation heat treatment and stress concentration phenomenon caused by nonmetallic sundries exceeding the standard and so on. Conclusion by improving the heat treatment process, optimizing the structure design and improving the machining accuracy, the tooth breaking phenomenon of 17CrNiMo6 gear shaft can be improved.
【作者单位】： 郑州电力高等专科学校;郑州电力机械厂;
【基金】：郑州电力高等专科学校科研项目(ZEPCKY2016-08)
【分类号】：TG115

【相似文献】

相关期刊论文 前10条

1 蒋金海;;断齿再植[J];锻压机械;1980年03期

2 龙礼;;锯条对接、裂纹、断齿的气焊与修复[J];木工机床;1988年02期

3 祝显民;减速机断齿原因分析及修复[J];大氮肥;2002年04期

4 刘庆兰;程里;王春莉;;齿轮轴断齿分析[J];理化检验(物理分册);2006年12期

5 高敏华;齿轮轴断齿失效分析[J];金属热处理;1994年09期

6 李运生;楼天明;许安心;;回转窑主减速机高速齿轮轴断齿、断轴分析与对策[J];浙江冶金;2014年01期

7 倪志华;郁超;马久;隋向军;;伞齿轮断齿现象的工艺分析[J];内蒙古农业大学学报(自然科学版);2006年03期

8 卫_";;42CrMo钢齿轮轴断齿原因分析[J];价值工程;2013年23期

9 樊咏川;罗兹风机断齿事故分析[J];中州建筑;1994年02期

10 ;薄板车间3米主减速机中速齿轮轴的断齿焊接[J];重型机械;1977年01期

相关会议论文 前2条

1 朱海琴;;齿轮断齿时的时频域特征和实例分析[A];河北冶金学会2013年度空分专业学术交流会论文集[C];2013年

2 宋敏华;;链轮断齿分析[A];2009年全国失效分析学术会议论文集[C];2009年

相关硕士学位论文 前2条

1 董国霞;汽车起动机在气体机应用环境下的断齿故障分析与优化设计研究[D];吉林大学;2016年

2 陈裴;船用行星齿轮断齿故障机理研究[D];上海交通大学;2014年

，

本文编号：1829315