基于XPS硬质合金刀具氧化磨损的试验分析
发布时间：2018-05-06 01:20
本文选题：XPS + 氧化磨损 ； 参考：《工具技术》2017年01期
【摘要】：采用多功能表面分析系统对车铣加工Ti6Al4V钛合金的硬质合金刀具进行X射线电子能谱分析(XPS)。通过对磨损区域进行全谱扫描和精细谱扫描,应用XPSPEAK4.1和Origin7.5对所得数据进行分峰拟合处理,最后分析了所生成的氧化物对刀具磨损和刀具寿命的影响。试验结果表明涂层材质为S30T的刀具磨损表面有Ti O_2、Al_2O_3、Co O和Ti N等物质生成;H13A非涂层材质刀具磨损表面有Ti O_2、WO3和Co_3O_4等氧化物生成。
[Abstract]:A multifunctional surface analysis system was used to analyze the X-ray electron spectroscopy (EDS) of cemented carbide tools for turning and milling Ti6Al4V titanium alloy. Through the full-spectrum scanning and fine spectrum scanning of the wear zone, the data were fitted by XPSPEAK4.1 and Origin7.5, and the influence of the oxide on the tool wear and tool life was analyzed. The experimental results show that the wear surface of the tool with S30T coating material has TIO _ s _ 2Al _ 2O _ 3Co _ O and Ti _ (N) non-coated cutting tool wear surface, and oxides such as TIO _ 2O _ 3 and Co_3O_4 are formed on the tool wear surface of H13A uncoated material.
【作者单位】： 沈阳理工大学;
【基金】：国家科技重大专项(2012ZX04003-061) 辽宁省教育厅一般项目(L2015463)
【分类号】：TG711
【相似文献】
相关期刊论文 前10条
1 李良福;硬质合金刀具的强化[J];硬质合金;2002年01期
2 ;传统车削技术的创新与山高新一代硬质合金刀具[J];工具技术;2004年09期
3 高永明;不断推陈出新的黛杰硬质合金刀具[J];航空制造技术;2005年07期
4 崔乐伟;;硬质合金刀具使用分析[J];西部探矿工程;2006年12期
5 ;刀具行业硬质合金刀具占比逐步增大[J];工具技术;2008年07期
6 刘远行;;硬质合金刀具使用要领[J];科技信息;2009年17期
7 李倩;;焊接式硬质合金刀具裂纹的产生及解决方案[J];航空制造技术;2011年14期
8 高宇顺;;硬质合金刀具在实习教学中的使用需求[J];职业;2011年29期
9 郭芬芳;;整体硬质合金刀具钝化的研制与应用[J];超硬材料工程;2012年04期
10 远;;欧美各国生产及挿售不重磨式硬质合金刀具的概况[J];工具技术;1966年03期
相关会议论文 前5条
1 孙卫权;杨慧敏;白佳声;;模具高速切削加工用硬质合金刀具材料[A];第十五届华东地区热处理年会暨华东地区热处理年会三十周年纪念活动论文摘要集[C];2006年
2 徐洋;初鑫;郝胜智;李e，
本文编号：1850148
本文链接：https://www.wllwen.com/kejilunwen/jiagonggongyi/1850148.html