5052铝合金光纤激光焊工艺

发布时间：2018-05-12 08:23

  本文选题：铝合金 + 光纤激光器　； 参考：《焊接》2017年08期

【摘要】：采用1 000 W单模光纤激光器对1 mm厚的5052铝合金进行焊接,对激光功率、焊接速度、离焦量三因素进行正交试验,得到最佳工艺参数为功率900 W,焊接速度100 mm/s,离焦量2 mm。对焊接接头进行拉升试验,结果表明,最佳工艺参数条件下焊接强度达到282 MPa,达到母材强度的72%。进一步对焊缝截面进行分析,焊缝完全熔透、内部无气孔且无材料缺失的情况下,焊接接头强度最高。
[Abstract]:1 000 W single mode fiber laser was used to weld 5052 aluminum alloy with a thickness of 1 mm. Three factors, laser power, welding speed and defocus, were tested by orthogonal experiments. The optimum process parameters were power 900W, welding speed 100mm / s, defocus 2 mm. The tensile test of welded joint shows that the welding strength reaches 282 MPA under the optimum process parameters and reaches 72% of the base metal strength. Further analysis of the weld section shows that the strength of the welded joint is the highest when the weld is fully permeable, with no porosity inside and no material missing.
【作者单位】： 无锡工艺职业技术学院;
【分类号】：TG456.7

【相似文献】

相关期刊论文 前10条

1 ;中国国产窄线宽光纤激光器取得重点突破[J];现代制造;2010年44期

2 吴国良;李建伟;郑志强;曹巍巍;;光纤激光多功能加工设备设计方案[J];内燃机;2012年03期

3 梁桂芳;焊缝重复返修对焊接接头强度的影响[J];造船技术;1990年03期

4 陈丽珑,李致焕,张锡爱;母材不等强焊接接头强度研究[J];焊接技术;2002年01期

5 蔡晋源;;关于提高钛-钢焊接接头强度的建议[J];科技风;2010年10期

6 屈金山，王元良，邓江;铝合金919焊接接头强度及硬度分析[J];机械工程材料;1994年05期

7 张伟民;覃启才;梁锡森;;轧后余热处理螺纹钢筋焊接接头强度[J];物理测试;1993年06期

8 李少华;尹士科;刘奇凡;;焊接接头强度匹配和焊缝韧性指标综述[J];焊接;2008年01期

9 薛河,吕涛,史耀武;焊接接头强度不等组配试样的三点弯曲试验[J];西安交通大学学报;1998年11期

10 马夏康,孙国有,陈志平,章烈;长颈铜法兰和铜管焊接接头强度试验研究[J];化工装备技术;1999年03期

相关会议论文 前1条

1 曹雷;宗培;胡毅军;李宁;;12Ni3CrMoV钢焊接接头强度匹配特征分析[A];第十一次全国焊接会议论文集（第2册）[C];2005年

相关硕士学位论文 前2条

1 仇毅;光纤激光抛光模具钢研究[D];北京工业大学;2015年

2 王丹丹;不锈钢和镀铜—镍低碳钢的激光点焊工艺及性能研究[D];华中科技大学;2016年

，

本文编号：1877871