退火露点对TWIP钢选择性氧化及可镀性的影响

发布时间：2018-05-12 10:18

  本文选题：TWIP钢 + 热镀锌　； 参考：《金属热处理》2017年02期

【摘要】：以TWIP钢为研究对象,在不同露点和温度下进行退火-镀锌试验,采用FE-SEM、EDS能谱仪和EPMA对退火试样进行分析,并与镀锌效果对照,得到退火气氛对可镀性的影响。试验结果表明:在两种退火温度下,露点为-50℃时,氧势低,极少量的Mn发生外氧化,热镀锌效果较好;随着露点升高,氧势升高,表面生成更多膜状和颗粒状Mn的氧化物,可镀性变差;而氧势足够高时,致使部分Mn发生内氧化,表面覆盖少量的块状Mn的氧化物,且有Al的氧化物出现,镀锌效果最好。
[Abstract]:Taking TWIP steel as the research object, the annealing galvanizing test was carried out at different dew points and temperatures. The annealed samples were analyzed by FE-SEMU EDS and EPMA, and compared with the galvanizing effect, the effect of annealing atmosphere on the plating property was obtained. The experimental results show that at two annealing temperatures, the oxygen potential is low and a very small amount of mn is oxidized out of the surface at -50 鈩，

本文编号：1878212