【摘要】：针对正交试验设计方法在工艺参数水平较多时,试验数量巨大,甚至无法进行的缺点,本文提出了利用均匀试验的方法来研究多水平工艺参数对C型钢成形质量的影响。先是采用MSC.Marc对C型钢的整体及各层的应力应变分布进行了分析。然后,将基于均匀试验设计获得的计算结果样本在MATLAB中对数据进行了回归分析,得到了优化的工艺参数。结果表明:合理的工艺参数能够降低板材成形的边部最大等效应变,有效改善了冷弯产品的质量。
[Abstract]:In view of the disadvantage of orthogonal design method that the number of experiments is too large or even unable to be carried out when the level of process parameters is high, a uniform test method is proposed to study the influence of multi-level process parameters on the forming quality of C section steel. First, MSC.Marc was used to analyze the stress and strain distribution of C section steel. Then, the data are regressed in MATLAB, and the optimized process parameters are obtained. The results show that reasonable process parameters can reduce the maximum equivalent strain of the edge of sheet metal forming and improve the quality of cold-formed products effectively.
【作者单位】： 宁波大学机械工程与力学学院;浙江省零件轧制成形技术研究重点实验室;中冶建筑研究总院有限公司;
【基金】：国家自然科学基金项目(51475247) 浙江省科技计划项目(2016C31018) 宁波市自然科学基金项目(2015A610099)
【分类号】：TG306

【相似文献】

相关期刊论文 前7条

1 胡海山;朱群英;左美玲;;均匀试验设计优化金银花总黄酮的提取[J];现代测量与实验室管理;2010年02期

2 崔蓉,苏利,王洪玮,赵京辉;均匀试验设计优化试验条件的研究-应用于分光光度法测定抗坏血酸[J];中国卫生检验杂志;2003年06期

3 李亚东,李爱勤,白宝丰,张宏英,王建莉,王晓磊;应用均匀试验设计研究ABS/PVC无溴阻燃配方[J];郑州轻工业学院学报;2003年02期

4 段晓颖;高卫芳;张辉;闫艳仓;吴彩丽;;均匀试验设计优选青黛提取工艺[J];中国现代应用药学;2012年04期

5 李梅,李志强;应用均匀试验设计研究PVC阻燃电缆料[J];工程塑料应用;2002年02期

6 章银良;;均匀试验设计在腌鱼工艺优化中的应用[J];食品科技;2008年09期

7 ;[J];;年期

相关会议论文 前2条

1 孙朝阳;吴梓新;;均匀试验设计方法对PTT合成工艺的研究[A];2012年全国高分子材料科学与工程研讨会学术论文集（上册）[C];2012年

2 易忠胜;刘树深;张爱茜;王连生;;基于均匀试验设计交叉检验的VSMP变量筛选方法[A];第五届全国环境化学大会摘要集[C];2009年

相关硕士学位论文 前2条

1 宋杰;均匀试验设计方法在土木工程中的应用研究[D];昆明理工大学;2011年

2 寇林元;均匀试验设计效果评价及优化分析方法研究[D];山西医科大学;2009年

，

本文编号：1886095