Q235钢薄板单点增量成形延性破损的有限元模拟

发布时间：2018-05-24 19:27

  本文选题：Q钢薄板 + 单点增量成形　； 参考：《机械工程材料》2017年03期

【摘要】：将损伤力学中的破损应变、三轴应力和应变比等参数作为Q235钢薄板出现延性破损的标准,以成形圆锥台件为例,运用ABAQUS有限元软件对Q235钢薄板单点增量成形的延性破损进行了有限元模拟,并进行了相关的试验验证。结果表明:在Q235钢薄板的成形区域上,板料的厚度分布不均匀;圆锥台件底部和顶部的厚度变化率呈对称分布,中部的厚度最薄,是最易出现延性破损的区域;模拟结果能较准确地预测出Q235钢薄板发生延性破损的位置,试验结果证明了所建有限元模型的正确性。
[Abstract]:The parameters of damage strain, triaxial stress and strain ratio in damage mechanics are taken as the criterion of ductile damage of Q235 steel sheet. The ductile failure of Q235 steel sheet in single point incremental forming was simulated by using ABAQUS finite element software, and the relevant tests were carried out. The results show that the thickness distribution of the sheet is not uniform in the forming area of Q235 steel sheet, the thickness change rate of the bottom and top of the cone plate is symmetrical distribution, and the thickness of the middle part is the thinnest, which is the most prone to ductile damage. The results of simulation can accurately predict the location of ductile failure of Q235 steel sheet. The experimental results prove the correctness of the finite element model.
【作者单位】： 西安理工大学机械与精密仪器工程学院;
【基金】：国家自然科学基金资助项目(51475366,51475146) 高等学校博士点基金资助项目(20116118110005)
【分类号】：TG306

【相似文献】

相关期刊论文 前2条

1 巩岩;赵磊;;单点金刚石机床及其在光学工程领域的应用[J];中国光学;2011年06期

2 ;[J];;年期

相关会议论文 前3条

1 张平松;刘盛东;吴荣新;;单点探测技术与应用[A];纪念矿井地质专业委员会成立二十周年暨矿井地质发展战略学术研讨会专辑[C];2002年

2 苑继超;郭万成;;单点除尘在承钢的应用[A];2010年全国冶金安全环保学术交流会论文集[C];2010年

3 王国强;李文坤;韦宝成;王洪芳;刘倩丽;尚景;;建造新技术在曹妃甸单点(CFD11-1 SPM)工程项目中的应用[A];2006年度海洋工程学术会议论文集[C];2006年

相关硕士学位论文 前3条

1 万方丽;多任务数据处理引擎资源共享与错误隔离机制研究[D];华中科技大学;2014年

2 邓玲;川西气田开采后期困难井单点增压工艺研究[D];西南石油大学;2015年

3 曹捚汇;单点渐进成形过程中成形缺陷的数值模拟研究[D];吉林大学;2010年

，

本文编号：1930268