磨料水射流切割微晶复合材料的工艺参数对光滑区粗糙度的影响

发布时间：2018-05-27 02:36

  本文选题：磨料水射流 + 微晶复合材料　； 参考：《硬质合金》2016年05期

【摘要】：本文通过单因素试验,研究了磨料水射流切割微晶复合材料时射流压力、靶距、切割速度和磨料流量对光滑区粗糙度的影响规律,进行了正交试验,得出了磨料水射流各工艺参数对光滑区粗糙度影响的重要程度主次顺序,并且得出了最优工艺参数组合。试验结果表明:在磨料水射流切割微晶复合材料时,射流压力增加,光滑区粗糙度先减小后增加;靶距增加,粗糙度增大;切割速度增加,粗糙度增大;磨料流量增加,粗糙度减小。优化后的加工工艺参数为:射流压力260 MPa、靶距4 mm、切割速度144mm/min、磨料流量590 g/min。
[Abstract]:In this paper , the influence of jet pressure , target distance , cutting speed and abrasive flow on the roughness of smooth zone was studied by single factor test , and the orthogonal test was carried out . The optimum technological parameters were obtained . The experimental results show that the jet pressure is increased , the roughness is increased , the roughness is increased , the roughness is increased , the roughness is increased , the cutting speed is increased , the roughness is increased and the roughness is reduced . The optimized processing parameters are as follows : jet pressure : 260 MPa , target distance 4 mm , cutting speed 144 mm / min , abrasive flow rate 590 g / min .
【作者单位】： 哈尔滨理工大学机械动力学院;
【基金】：黑龙江省教育厅科学技术项目(项目编号):12531126
【分类号】：TG664

【相似文献】

相关期刊论文 前10条

1 赵民,赵永赞,刘黎,谢国良,蒲永伟;磨料水射流切割石材的应用研究[J];金刚石与磨料磨具工程;2000年02期

2 赵永赞,吴玉厚,富大伟,赵民,王海波;后混合磨料水射流切割石材的特性[J];河北理工学院学报;2002年02期

3 苏卫民;磨料水射流切割技术[J];大众科技;2004年08期

4 杨丽君;;磨料水射流切割技术[J];淮北职业技术学院学报;2009年05期

5 吴海;刘波;王国涛;何红阳;;磨料水射流切割技术分析及研究[J];机械管理开发;2010年04期

6 董星;王瑞宏;;磨料水射流切割技术[J];机械工程师;1993年05期

7 邹正龙;磨料水射流切割煤岩的机理研究[J];煤;1996年02期

8 宫平,王pち，

本文编号：1940079